Описание материалов:
Menzolit® BMC 2910 is a bulk moulding compound based on unsaturated polyester resin. The product is glass fibre reinforced and contains mineral fillers. In case of fire the product doesn't melt, neither does it form droplets nor is smoke generation excessive. The material is injection moulded in heated steel moulds. It is recommended to work with chrome plated tools. The product contains no halogens nor any heavy metals.
Menzolit® BMC 2910 incorporates additives which enhance the integral performance of mouldings during and after fire, currently used to mould Boltcaps which are designed to provide protection to the bolted connections in structural steel frames of buildings in the event of fire.Boltcaps are designed to insulate the bolts from temperature of the fire (1000° C) and stop embrittlement and fracture resulting in building collapse.The boltcap also protects against a too rapid cooling and failure of the bolt due to quenching from Firemen's water hoses.
| Главная Информация | |
|---|
| Наполнитель/армирование | - Стекло \ Mineral, 13% наполнитель по весу
|
| Характеристики | - Без галогенов
- Низкий уровень дыма
|
| Внешний вид | |
| Метод обработки | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Плотность | 1.95 | g/cm³ | ISO 1183 |
| Формовочная усадка | | | |
| -- 1 | 0.0 | % | DIN 53464 |
| -- | 0.050 | % | ISO 2577 |
| Поглощение воды (23°C, 24 hr) | < 0.50 | % | ISO 62 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Модуль растяжения | 13000 | MPa | ISO 527-4 |
| Tensile Stress (Break) | 30.0 | MPa | ISO 527-4 |
| Флекторный модуль | 11000 | MPa | ISO 178 |
| Флекторный стресс | 80.0 | MPa | ISO 14125 |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Charpy Unnotched Impact Strength | 20 | kJ/m² | ISO 179 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | > 200 | °C | ISO 75-2/A |
| Температура непрерывного использования | 165 | °C | |
| Температура перехода стекла | 170 | °C | ISO 11357-2 |
| CLTE-
Поток | 1.2E-5 | cm/cm/°C | ISO 11359-2 |
| Электрический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельное сопротивление поверхности | 1.0E+12 | ohms | IEC 60093 |
| Сопротивление громкости | 1.0E+15 | ohms·cm | IEC 60093 |
| Воспламеняемость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Индекс кислорода | 27 | % | ISO 4589-2 |
| Дополнительная информация | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Содержание волокна | 13 | % | ISO 1172 |
| Обозначение материала | >UP-(MD+GF)88< | | EN 14598-1 |
| Инъекция | Номинальное значение | Единица измерения | |
|---|
| Температура формы | 135 to 150 | °C | |
| Давление впрыска | 8.00 to 10.0 | MPa | |
| Примечание |
|---|
| 1 . | Post Molding Shrinkage |