LUVOCOM® 50-8472/BL

Категория	PC, Polycarbonate
Производитель	Lehmann & Voss & Co.
Торговая марка	LUVOCOM®
Порт	Китай Шанхайский порт
Торговые условия	FOB, CFR, CIF
Платежное средство	L/C, T/T, Western Union
PDF	fzEUdz_LUVOCOM-50-8472-BL.pdf
Контактная информация	EMAIL US  sales@su-jiao.com Служба поддержки клиентов Вичат

Описание материалов:

LUVOCOM®50-8472/BL is a polycarbonate (PC) material,. This product is available in Europe,. LUVOCOM®The main characteristics of 50-8472/BL are: good dimensional stability.

Typical application areas include:

engineering/industrial accessories

Tools

business/office supplies

food contact applications

Sporting goods

Главная Информация
Характеристики	Хорошая стабильность размеров
Используется	Неспецифическое применение пищи Инженерные аксессуары Машина/механические детали Бизнес-оборудование Спортивные товары Медицинские принадлежности/принадлежности для ухода Литьевая форма/инструмент
Внешний вид	Синий

Физический	Номинальное значение	Единица измерения	Метод испытания
Плотность	1.68	g/cm³	ISO 1183
Плавкий объем-расход (MVR) (300°C/2.16 kg)	45.0	cm³/10min	ISO 1133
Формовочная усадка	0.50 - 0.80	%	DIN 16901
Поглощение воды (23°C, 24 hr)	< 0.20	%

Механические	Номинальное значение	Единица измерения	Метод испытания
Модуль растяжения	4000	MPa	ISO 527-2
Tensile Stress (Break)	55.0	MPa	ISO 527-2
Растяжимое напряжение (Yield)	4.0	%	ISO 527-2
Флекторный модуль	3400	MPa	ISO 178
Флекторный стресс	80.0	MPa	ISO 178
Flexural Strain at Flexural Strength	5.0	%	ISO 178

Тепловой	Номинальное значение	Единица измерения	Метод испытания
Максимальная рабочая температура- Короткий срок	150	°C

Электрический	Номинальное значение	Единица измерения	Метод испытания
Insulation Resistance	> 1.0E+12	ohms	IEC 60167

Воздействие	Номинальное значение	Единица измерения	Метод испытания
Charpy Unnotched Impact Strength (23°C)	45	kJ/m²	ISO 179/1eU

Тепловой	Номинальное значение	Единица измерения	Метод испытания
Температура непрерывного использования	130	°C	UL 746B

Электрический	Номинальное значение	Единица измерения	Метод испытания
Удельное сопротивление поверхности	> 1.0E+12	ohms	IEC 60093

Инъекция	Номинальное значение	Единица измерения
Температура сушки	120	°C
Время сушки	4.0 - 6.0	hr
Рекомендуемая максимальная влажность	0.020	%
Задняя температура	280 - 300	°C
Средняя температура	290 - 310	°C
Передняя температура	300 - 320	°C
Температура сопла	290 - 310	°C
Температура обработки (расплава)	295	°C
Температура формы	80.0 - 120	°C

Инструкции по впрыску
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing, the moisture level should not exceed 0.02%, otherwise molecular degradation may occur. Suitable heat treatment may increase resistance to the formation of stress cracks. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Инструкции по впрыску

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing, the moisture level should not exceed 0.02%, otherwise molecular degradation may occur. Suitable heat treatment may increase resistance to the formation of stress cracks. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Тип материала	Категория	Производитель
Spartech Polycom SC7-7006F	PC	Spartech Polycom
HOPELEX PCG-2205	PC	Lotte Chemical Corporation
Hylex® P1017 L2 HB	PC	Entec Polymers
CALIBRE™ 302EP-22	PC	Trinseo
LEXAN™ LUX2910T_ resin	PC	SABIC Innovative Plastics Europe
LEXAN™ FST9705 resin	PC	SABIC Innovative Plastics