LUVOCOM® 2205-7123 VP

Категория	PAEK, Polyaryletherketone
Производитель	Lehmann & Voss & Co.
Торговая марка	LUVOCOM®
Порт	Китай Шанхайский порт
Торговые условия	FOB, CFR, CIF
Платежное средство	L/C, T/T, Western Union
PDF	fs894K_LUVOCOM-2205-7123-VP.pdf
Контактная информация	EMAIL US  sales@su-jiao.com Служба поддержки клиентов Вичат

Описание материалов:

LUVOCOM®2205-7123 VP is a polyaryl ketone (PAEK) material, which contains a carbon fiber reinforced material. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,.

LUVOCOM®The main features of 2205-7123 VP are:

sterilizable

Good dimensional stability

chemical resistance

Heat resistance

Lubrication

LUVOCOM®The typical application areas of 2205-7123 VP are: medical/health care

Главная Информация
Наполнитель/армирование	Армированный материал из углеродного волокна
Добавка	Ptfe лубрикант
Характеристики	Хорошая стабильность размеров Хорошая химическая стойкость Теплостойкость, высокая Сопротивление гидролизу Смазка Стабильность гидролиза Паровая дезинфекция
Используется	Медицинские принадлежности/принадлежности для ухода
Внешний вид	Темно-серый

Физический	Номинальное значение	Единица измерения	Метод испытания
Плотность	1.47	g/cm³	ISO 1183
Массовый расход расплава (MFR) (380°C/10.0 kg)	18	g/10 min	ISO 1133
Формовочная усадка	0.10 - 0.40	%	DIN 16901

Механические	Номинальное значение	Единица измерения	Метод испытания
Модуль растяжения	13000	MPa	ISO 527-2
Tensile Stress (Break)	145	MPa	ISO 527-2
Растяжимое напряжение (Yield)	1.8	%	ISO 527-2
Флекторный модуль	11000	MPa	ISO 178
Флекторный стресс	215	MPa	ISO 178
Коэффициент трения
Dynamic	0.32
Static	0.29
Flexural Strain at Flexural Strength	2.3	%	ISO 178

Тепловой	Номинальное значение	Единица измерения	Метод испытания
Максимальная рабочая температура- Короткий срок	250	°C

Электрический	Номинальное значение	Единица измерения	Метод испытания
Insulation Resistance		ohms	IEC 60167

Воздействие	Номинальное значение	Единица измерения	Метод испытания
Ударная прочность (23°C)	6.0	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength (23°C)	26	kJ/m²	ISO 179/1fU

Тепловой	Номинальное значение	Единица измерения	Метод испытания
Температура непрерывного использования	220	°C	UL 746B
Викат Температура размягчения	280	°C	ISO 306

Инъекция	Номинальное значение	Единица измерения
Температура сушки	150	°C
Время сушки	3.0 - 6.0	hr
Рекомендуемая максимальная влажность	0.050	%
Задняя температура	360 - 370	°C
Средняя температура	370 - 380	°C
Передняя температура	380 - 390	°C
Температура сопла	360 - 380	°C
Температура обработки (расплава)	390	°C
Температура формы	160 - 180	°C

Инструкции по впрыску
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing, the moisture content should not exceed 0.05%. To avoid internal stresses, a medium to high injection rate should be used. An increase in tool temperature may be helpful. The parts may be tempered at a later stage to reduce internal stresses. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. High-temperature polymers place increased demands on the tool steels employed. Please contact us for further information.

Инструкции по впрыску

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing, the moisture content should not exceed 0.05%. To avoid internal stresses, a medium to high injection rate should be used. An increase in tool temperature may be helpful. The parts may be tempered at a later stage to reduce internal stresses. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. High-temperature polymers place increased demands on the tool steels employed. Please contact us for further information.

Тип материала	Категория	Производитель
AvaSpire® AV-481	PAEK	Solvay Specialty Polymers
Pyramid™ KK2219	PAEK	Polymics, Ltd.
Arylmax® K7500GF30	PAEK	Polymics, Ltd.
RTP 3807	PAEK	RTP Company
RTP 3803	PAEK	RTP Company
LUVOCOM® 1114-0717	PAEK	Lehmann & Voss & Co.

Получите информацию об этом продукте следующим способом.

Телефон	+086 13424755533
EMAIL US	sales@su-jiao.com
Служба поддержки клиентов Вичат

