MAGNUM ABS resins are thermoplastic materials which provide an excellent balance of processability, impact resistance and heat resistance as imparted by the various polymer compositions. MAGNUM ABS resins are available in a wide range of melt flow rates, impact strength and heat resistance for both high and low gloss applications manufactured by injection molding, sheet or profile extrusion and thermoforming processes.
Automotive MAGNUM ABS resins offer a wide range of gloss, viscosity, impact strength and heat properties for use in numerous automotive applications. Melt flow rates from 1 to 12 g/10 min, impact strengths from 2.4 to 11 ft-lb/in and heat distortion temperatures from 171°F to 194°F are available. Available primarily as natural plus concentrates, MAGNUM ABS resins are used in a wide variety of automotive applications including structural instrument panels, consoles, pillars, and exterior trim parts requiring painting and plating.
MAGNUM 347 EZ ABS resin is a higher flow version of 342 EZ having slightly lower impact strength. The melt flow rate of approximately 12 g/10min is often suitable for parts with long flow lines and minimal impact requirements.
Главная Информация
Характеристики
Хорошая технологичность
Высокая термостойкость
Средняя ударопрочность
Используется
Автомобильные Приложения
Детали конструкции
Формы
Гранулы
Метод обработки
Литье под давлением
Экструзионный профиль
Экструзионный лист
Термоформовка
Физический
Номинальное значение
Единица измерения
Метод испытания
Удельный вес
--
1.04
g/cm³
ASTM D792
--
1050
kg/m³
ISO 1183 1
Массовый расход расплава (MFR) (230°C/3.8 kg)
12
g/10 min
ASTM D1238
Плавкий объем-расход (220°C/10.0 kg)
43.0
cm³/10min
ISO 1133 2
Формовочная усадка-
Поток
0.40 to 0.70
%
ASTM D955
Механические
Номинальное значение
Единица измерения
Метод испытания
Модуль растяжения
--3
2070
MPa
ASTM D638
--
1890
MPa
ISO 527-2 4
Прочность на растяжение
Yield5
41.4
MPa
ASTM D638
Yield
34.0
MPa
ISO 527-2 6
Удлинение при растяжении
Yield7
2.5
%
ASTM D638
Yield
2.2
%
ISO 527-2 8
Break9
30
%
ASTM D638
Номинальное напряжение при разрыве
> 50
%
ISO 527-2 10
Флекторный модуль 11
2170
MPa
ASTM D790
Flexural Strength 12
65.5
MPa
ASTM D790
Воздействие
Номинальное значение
Единица измерения
Метод испытания
Ударная прочность
ISO 179/1eA 13
-30°C
5.00
kJ/m²
23°C
8.00
kJ/m²
Ударная сила Шарпи
ISO 179/1eU 14
-30°C
90.0
kJ/m²
23°C
140
kJ/m²
Зубчатый изод Impact 15(23°C, 3.20 mm)
130
J/m
ASTM D256
Ударное устройство для дротиков 16
ASTM D3763
23°C, 3.20 mm, Peak Energy
28.2
J
23°C, 3.20 mm, Total Energy
35.0
J
Тепловой
Номинальное значение
Единица измерения
Метод испытания
Температура отклонения при нагрузке
0.45 MPa, Unannealed, 3.20 mm
85.0
°C
ASTM D648
0.45 MPa
88.0
°C
ISO 75-2 17
1.8 MPa, Unannealed, 3.20 mm
73.9
°C
ASTM D648
1.8 MPa
77.0
°C
ISO 75-2 18
Викат Температура размягчения
--
102
°C
ASTM D1525
50°C/h, B (50N)
94.0
°C
ISO 306 19
CLTE-
Поток
7.6E-5
cm/cm/°C
ISO 11359-2 20
Инъекция
Номинальное значение
Единица измерения
Температура сушки
82.2 to 85.0
°C
Время сушки
2.0 to 4.0
hr
Рекомендуемая максимальная влажность
0.10
%
Температура обработки (расплава)
216 to 232
°C
Температура формы
26.7 to 48.9
°C
Back Pressure
0.345 to 3.45
MPa
Тонаж зажима
2.8 to 4.1
kN/cm²
Отношение винта L/D
20.0:1.0
Коэффициент сжатия винта
1.5:1.0 to 3.5:1.0
Примечание
1 .
Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
2 .
Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
3 .
Type I, 51 mm/min
4 .
Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
5 .
Type I, 51 mm/min
6 .
Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
7 .
Type I, 51 mm/min
8 .
Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
9 .
Type I, 51 mm/min
10 .
Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
11 .
Type I, 1.3 mm/min
12 .
Type I, 1.3 mm/min
13 .
Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
14 .
Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
15 .
0.25 mm Notch Depth
16 .
3.39 m/sec
17 .
Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
18 .
Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
19 .
Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
20 .
Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.