Vydyne R413H NT is general-purpose, heat-stabilized, impact-modified, 13% glass-fiber reinforced PA66 resin. Available in natural, It is specifically designed to maximize toughness, while retaining physical properties. This product is also lubricated for improved flow and offers superior surface appearance.
Glass-fiber reinforced Vydyne resins provide higher heat distortion temperature, resistance to creep and better dimensional stability when compared with unreinforced PA66. These products have good chemical resistance to a broad range of chemicals including gasoline, hydraulic fluids and most solvents.
Typical Applications/End Uses:
Vydyne R413H NT is successfully used in a wide range of injection-molding engineering applications, including automotive clips, fasteners, brackets and carbon canisters; electrical connectors, housings, bobbins, etc.; and industrial gears, bearing shells, covers, housings, etc.
| Главная Информация | |
|---|
| Наполнитель/армирование | - Стекловолокно, 13% наполнитель по весу
|
| Добавка | |
| Характеристики | - Сопротивление бензину
- Хорошая химическая стойкость
- Хорошее сопротивление ползучести
- Хорошая стабильность размеров
- Хороший поток
- Хорошая ударопрочность
- Хороший выпуск пресс-формы
- Устойчивость к смазке
- Высокая жесткость
- Высокая прочность
- Высокая прочность на растяжение
- Смазка
- Маслостойкий
- Устойчивость к растворителям
|
| Используется | - Автомобильная крышка под капот
- Шестерни
- Корпуса
- Оборудование для газонов и сада
- Электропитание/другие инструменты
|
| Рейтинг агентства | - Астм д 4066 PA0161G15
- Астм д 6779 PA0161G15
|
| Номер файла UL | |
| Внешний вид | |
| Формы | |
| Метод обработки | |
| Физический | Сухой | Состояние | Единица измерения | Метод испытания |
|---|
| Плотность | 1.21 | -- | g/cm³ | ISO 1183 |
| Формовочная усадка | | | | ISO 294-4 |
| Across Flow
: 23°C, 2.00 mm | 0.80 | -- | % | |
| Flow
: 23°C, 2.00 mm | 0.70 | -- | % | |
| Поглощение воды | | | | ISO 62 |
| 23°C, 24 hr | 1.0 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.9 | -- | % | |
| Механические | Сухой | Состояние | Единица измерения | Метод испытания |
|---|
| Модуль растяжения (23°C) | 5500 | 4100 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 110 | 80.0 | MPa | ISO 527-2 |
| Растяжимое напряжение (Break, 23°C) | 5.0 | 13 | % | ISO 527-2 |
| Флекторный модуль (23°C) | 4800 | 2800 | MPa | ISO 178 |
| Флекторный стресс (23°C) | 140 | 73.0 | MPa | ISO 178 |
| Poisson's Ratio | 0.40 | -- | | ISO 527-2 |
| Воздействие | Сухой | Состояние | Единица измерения | Метод испытания |
|---|
| Ударная прочность | | | | ISO 179 |
| -40°C | 5.0 | 5.0 | kJ/m² | |
| -30°C | 6.0 | 10 | kJ/m² | |
| 23°C | 12 | 18 | kJ/m² | |
| Charpy Unnotched Impact Strength | | | | ISO 179 |
| -30°C | 80 | 70 | kJ/m² | |
| 23°C | 75 | 76 | kJ/m² | |
| Зубчатый изод ударная прочность | | | | ISO 180 |
| -40°C | 9.0 | 9.0 | kJ/m² | |
| -30°C | 10 | 10 | kJ/m² | |
| 23°C | 12 | 21 | kJ/m² | |
| Тепловой | Сухой | Состояние | Единица измерения | Метод испытания |
|---|
| Heat Deflection Temperature | | | | |
| 0.45 MPa, Unannealed | 258 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 235 | -- | °C | ISO 75-2/A |
| Температура плавления | 260 | -- | °C | ISO 11357-3 |
| CLTE | | | | ISO 11359-2 |
| Flow
: 23 to 55°C, 2.00 mm | 3.0E-5 | -- | cm/cm/°C | |
| Transverse
: 23 to 55°C, 2.00 mm | 1.1E-4 | -- | cm/cm/°C | |
| Электрический | Сухой | Состояние | Единица измерения | Метод испытания |
|---|
| Сопротивление громкости (0.750 mm) | 1.0E+9 | -- | ohms·cm | IEC 60093 |
| Диэлектрическая прочность (1.00 mm) | 3.0 | -- | kV/mm | IEC 60243 |
| Дуговое сопротивление (3.00 mm) | PLC 6 | -- | | ASTM D495 |
| Comparative Tracking Index (3.00 mm) | 400 to 599 | -- | V | IEC 60112 |
| Высокоусиленное дуговое зажигание (HAI) | | | | UL 746 |
| 0.400 mm | PLC 1 | -- | | |
| 0.750 mm | PLC 1 | -- | | |
| 1.50 mm | PLC 1 | -- | | |
| 3.00 mm | PLC 1 | -- | | |
| Высоковольтная скорость отслеживания дуги (HVTR) | PLC 3 | -- | | UL 746 |
| Зажигание горячей проволоки (HWI) | | | | UL 746 |
| 0.400 mm | PLC 4 | -- | | |
| 0.750 mm | PLC 4 | -- | | |
| 1.50 mm | PLC 4 | -- | | |
| 3.00 mm | PLC 4 | -- | | |
| Воспламеняемость | Сухой | Состояние | Единица измерения | Метод испытания |
|---|
| Огнестойкость | | | | UL 94 |
| 0.750 mm | HB | -- | | |
| 1.50 mm | HB | -- | | |
| 3.00 mm | HB | -- | | |
| Инъекция | Сухой | Единица измерения | |
|---|
| Температура сушки | 80.0 | °C | |
| Время сушки | 4.0 | hr | |
| Рекомендуемый Макс измельчения | 25 | % | |
| Задняя температура | 280 to 310 | °C | |
| Средняя температура | 280 to 310 | °C | |
| Передняя температура | 280 to 310 | °C | |
| Температура сопла | 280 to 310 | °C | |
| Температура обработки (расплава) | 285 to 305 | °C | |
| Температура формы | 65.0 to 95.0 | °C | |