Quadrant EPP Delrin® AF Blend
Описание материалов:
Delrin* AF Blend acetal is a unique thermoplastic material for use in moving parts in which low friction and long wear are important. It is a combination of Teflon* fibers uniformly dispersed in Delrin acetal resin. This combination produces a material that has strength, toughness, dimensional stability and good machinability, plus improved wear characteristics over unfilled Delrin. Delrin AF Blend, most commonly supplied as a 2:1 blend of Delrin AF100 and Delrin 150 resins, has excellent sliding/friction properties. Bearings made of Delrin AF Blend sustain high loads when operating at high speeds and show reduced wear. These bearings are also essentially free of slip-stick behavior because the static and dynamic coefficient of friction are closer than with most plastics. Delrin AF Blend retains much of the strength that is inherent in unmodified Delrin acetal. Some properties are changed due to the addition of the softer Teflon fiber. The natural color of Delrin AF Blend is dark brown.
Data provided by Quadrant Engineering Plastic Products from tests on stock shapes and parts produced by Quadrant EPP.
| Главная Информация | |
|---|
| Наполнитель/армирование | |
| Характеристики | - Устойчивость к воздействию алкоголя
- Щелочестойкие
- Хорошая стабильность размеров
- Хорошая прочность
- Хорошая прочность
- Хорошая износостойкость
- Устойчивость к углеводородам
- Низкое трение
- Низкая комбинация
- Обрабатываемый
|
| Используется | |
| Внешний вид | |
| Метод обработки | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 1.50 | g/cm³ | ASTM D792 |
| Поглощение воды | | | ASTM D570 |
| 24 hr | 0.20 | % | |
| Saturation | 1.0 | % | |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость Роквелла | | | ASTM D785 |
| M-Scale | 85 | | |
| R-Scale | 115 | | |
| Твердость дюрометра (Shore D) | 83 | | ASTM D2240 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Модуль растяжения | 3000 | MPa | ASTM D638 |
| Прочность на растяжение (Ultimate) | 55.2 | MPa | ASTM D638 |
| Удлинение при растяжении (Break) | 15 | % | ASTM D638 |
| Флекторный модуль | 3070 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 82.7 | MPa | ASTM D790 |
| Компрессионный модуль | 2410 | MPa | ASTM D695 |
| Прочность на сжатие (10% Strain) | 110 | MPa | ASTM D695 |
| Прочность сдвига | 52.4 | MPa | ASTM D732 |
| Коэффициент трения (vs. Steel - Static) | 0.19 | | Internal Method |
| Коэффициент износа | 120 | 10^-8 mm³/N·m | ASTM D3702 |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Зубчатый изод Impact | 37 | J/m | ASTM D256A |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Температура отклонения при нагрузке (1.8 MPa, Unannealed) | 118 | °C | ASTM D648 |
| Максимальная температура использования-
Долгосрочный, воздушный | 82 | °C | |
| Дополнительная информация | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Limiting Pressure Velocity 1 | 0.291 | MPa·m/s | Internal Method |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Пиковая температура кристаллизации (DSC) | 175 | °C | ASTM D3418 |
| CLTE-
Поток 2(-40 to 149°C) | 9.0E-5 | cm/cm/°C | ASTM E831 |
| Электрический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельное сопротивление поверхности 3 | > 1.0E+13 | ohms | Internal Method |
| Диэлектрическая прочность 4 | 16 | kV/mm | ASTM D149 |
| Диэлектрическая постоянная (1 MHz) | 3.10 | | ASTM D150 |
| Коэффициент рассеивания (1 MHz) | 0.010 | | ASTM D150 |
| Воспламеняемость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Огнестойкость (3.18 mm, Estimated Rating) | HB | | UL 94 |
| Примечание |
|---|
| 1 . | 4:1 safety factor |
| 2 . | 68°F |
| 3 . | EOS/ESD S11.11 |
| 4 . | Method A (Short-Time) |