Bayflex® XGT-100 (15% Glass)
Описание материалов:
Bayflex XGT-100 is an elastomeric polyurethane system used in the reaction injection molding (RIM) process. The system is supplied as two liquid components: Component A is a modified diphenylmethane diisocyanate (MDI), and Component B is a polyether polyol system.
The extended gel time of Bayflex XGT-100 system gives equipment designers the flexibility to create large, complex parts that can be molded on existing injection machinery. The resin 's excellent surface quality and high impact resistance make it a candidate for agricultural equipment, heavy-duty trucks, specialty transportation, and marine applications. As with any product, use of the Bayflex XGT-100 system in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability.
| Главная Информация | |
|---|
| Наполнитель/армирование | - Армированный стекловолокном материал, 15% наполнитель по весу
|
| Характеристики | - Высокая ударопрочность
- Отличный внешний вид
|
| Используется | - Применение корабля
- Сельскохозяйственное применение
|
| Формы | |
| Метод обработки | - Литье под давлением реакции (обод)
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 1.15 | g/cm³ | ASTM D792, ASTM D1622 |
| Формовочная усадка-
Поток (3.18 mm) | 0.55 - 0.65 | % | Internal method |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость дюрометра (Shore D, 3.18 mm) | 73 | | ASTM D2240 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Прочность на растяжение (Break, 3.18 mm) | 28.3 | MPa | ASTM D638 |
| Удлинение при растяжении (Break, 3.18 mm) | 50 | % | ASTM D638 |
| Флекторный модуль | | | ASTM D790 |
| -30°C, 3.18 mm | 2760 | MPa | ASTM D790 |
| 23°C, 3.18 mm | 1450 | MPa | ASTM D790 |
| 70°C, 3.18 mm | 655 | MPa | ASTM D790 |
| Эластомеры | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Tear Strength 1(3.18 mm) | 119 | kN/m | ASTM D624 |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Зубчатый изод Impact (3.18 mm) | 210 | J/m | ASTM D256 |
| Ударное устройство для дротиков 2 | | | ASTM D3763 |
| -30°C, 3.18 mm | 2.71 | J | ASTM D3763 |
| 23°C, 3.18 mm | 5.42 | J | ASTM D3763 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| CLTE-
Поток (3.18 mm) | 5.0E-5 | cm/cm/°C | ASTM D696 |
| Термокомплект | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Компоненты термокомплекта 3 | | | |
| Component a | Mixing ratio by weight: 150, mixing ratio by capacity: 130 | | |
| Component B | Mixing ratio by weight: 100, mixing ratio by capacity: 100 | | |
| Время демолд | 1.5 | min | |
| Дополнительная информация | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Нагрев-
4 в навесе 4(121°C, 3.18 mm) | 1.09 | cm | ASTM D3769 |
| Part A
Type: Isocyanate
Appearance: Light yellow to yellow liquid
Specific Gravity @ 25°C: 1.21
Viscosity @25°C: 700 mPa-s
Flash Point PMCC: 213 °C
NCO: 22.6 - 23.1 %
Part B
Type: Polyol
Appearance: Colorless to pale yellow liquid
Specific Gravity @ 25°C: 1.03
Viscosity @25°C: 550 mPa-s
Flash Point PMCC: 110 °C
Water: <0.09 wt%
Molding Parameters
Material Temperature - Component B: 43 to 49 °C
Mold Temperature: 66 to 71 °C
Polyol Nucleation - Specific Gravity: 0.90
shot time: 5 sec |
| Примечание |
|---|
| 1 . | C mould |
| 2 . | 2.24 m/sec |
| 3 . | 1.05 Index |
| 4 . | 1 hr |