Описание материалов:
Bayflex MP-25,000 is a solid elastomer which has a flexural modulus of 25,000 psi (172 MPa) at room temperature.* It is processed on reaction injection molding (RIM) equipment and is used for rollers, gaskets, and encapsulated windows. This system combines rapid demold times, excellent integrity at demold, improved release characteristics and outstanding physical properties. As with any product, use of the Bayflex MP-25,000 system in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability.
Bayflex MP-25,000 is a formulated RIM system supplied as two liquid components. Component A is a diphenylmethane diisocyanate (MDI) prepolymer, and Component B is a polyether polyol. Note: Component B should be agitated thoroughly prior to transfer of contents from the drum to the day tank.
| Главная Информация | |
|---|
| Характеристики | - Хорошая производительность при потере
|
| Используется | |
| Формы | |
| Метод обработки | - Литье под давлением реакции (обод)
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 1.04 | g/cm³ | ASTM D792, ASTM D1622 |
| Формовочная усадка-
Поток (3.00 mm) | 1.5 | % | Internal method |
| Поглощение воды (24 hr, 3.00 mm) | 3.3 | % | Internal method |
| Скорость поглощения воды-
240 hr (3.00 mm) | 5.0 | % | Internal method |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Низкая температура ломкости (-50°C, 3.00 mm) | No Cracking | | ASTM D746 |
| Дополнительная информация | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Погружение в воду, увеличение длины (3.00 mm) | 1.4 | % | Internal method |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость дюрометра (shaw d, 3.00mm) | 50 | | ASTM D2240 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Прочность на растяжение (Break, 3.00 mm) | 24.1 | MPa | ASTM D638 |
| Флекторный модуль | | | ASTM D790 |
| -30°C, 3.00 mm | 441 | MPa | ASTM D790 |
| 23°C, 3.00 mm | 172 | MPa | ASTM D790 |
| 65°C, 3.00 mm | 124 | MPa | ASTM D790 |
| Эластомеры | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Tensile Stress | | | ASTM D412 |
| 20% strain 1 | 7.93 | MPa | ASTM D412 |
| 50% strain, 3.00mm 2 | 8.27 | MPa | ASTM D412 |
| 100% strain, 3.00mm 3 | 9.65 | MPa | ASTM D412 |
| Прочность на растяжение (Break, 3.00 mm) | 24.1 | MPa | ASTM D412 |
| Удлинение при растяжении (Break, 3.00 mm) | 250 | % | ASTM D412 |
| Tear Strength 4(3.00 mm) | 85.8 | kN/m | ASTM D624 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| CLTE-
Поток (3.00 mm) | 1.4E-4 | cm/cm/°C | ASTM D696 |
| Термокомплект | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Компоненты термокомплекта 5 | | | |
| Component a | Mixing ratio by weight: 48 | | |
| Component B | Mixing ratio by weight: 100 | | |
| Срок годности (30°C) | 26 | wk | |
| Время демолд | 0.50 | min | |
| Дополнительная информация | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Part A
Type: Isocyanate
Specific Gravity @ 25°C: 1.21
Viscosity @25°C: 700 mPa-s
Flash Point PMCC: 213 °C
Part B
Type: Polyol
Specific Gravity @ 25°C: 1.03
Viscosity @25°C: 1200 mPa-s
Flash Point PMCC: 193 °C
Molding Parameters
Material Temperature: 32 to 42 °C
Mold Temperature: 65 to 75 °C |
| Примечание |
|---|
| 1 . | Die C, 510 mm/min |
| 2 . | C mold, 510mm/min |
| 3 . | Mouth die C, 510mm/min |
| 4 . | C mould |
| 5 . | 105 Index |