Описание материалов:

LUVOCOM®1106-8380/WT is a polyetherimide (PEI) material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,.

LUVOCOM®The main features of 1106-8380/WT are:

flame retardant/rated flame

Flame Retardant

Good dimensional stability

Heat resistance

Главная Информация
Характеристики	Хорошая стабильность размеров Теплостойкость, высокая Огнестойкий
Внешний вид	Кремовый цвет

Физический	Номинальное значение	Единица измерения	Метод испытания
Плотность	1.43	g/cm³	ISO 1183
Формовочная усадка	0.40 - 0.80	%	DIN 16901
Поглощение воды (23°C, 24 hr)	< 0.30	%

Механические	Номинальное значение	Единица измерения	Метод испытания
Модуль растяжения	3500	MPa	ISO 527-2
Tensile Stress (Break)	115	MPa	ISO 527-2
Растяжимое напряжение (Yield)	6.2	%	ISO 527-2
Флекторный модуль	3000	MPa	ISO 178
Флекторный стресс	155	MPa	ISO 178
Flexural Strain at Flexural Strength	7.5	%	ISO 178

Электрический	Номинальное значение	Единица измерения	Метод испытания
Insulation Resistance	> 1.0E+12	ohms	IEC 60167

Воздействие	Номинальное значение	Единица измерения	Метод испытания
Ударная прочность (23°C)	5.0	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength (23°C)	90	kJ/m²	ISO 179/1eU

Тепловой	Номинальное значение	Единица измерения	Метод испытания
Heat Deflection Temperature (1.8 MPa, Unannealed)	200	°C	ISO 75-2/A
Температура непрерывного использования	170	°C	UL 746B

Электрический	Номинальное значение	Единица измерения	Метод испытания
Удельное сопротивление поверхности	> 1.0E+12	ohms	IEC 60093

Воспламеняемость	Номинальное значение	Единица измерения	Метод испытания
Огнестойкость ¹	V-0		UL 94

Инъекция	Номинальное значение	Единица измерения
Температура сушки
Hot air dryer, A	120	°C
Hot air dryer, B	150	°C
Время сушки
Hot air dryer, A	> 8.0	hr
Hot air dryer, B	> 4.0	hr
Задняя температура	330 - 350	°C
Средняя температура	340 - 390	°C
Передняя температура	350 - 400	°C
Температура сопла	350 - 400	°C
Температура обработки (расплава)	380	°C
Температура формы	150 - 180	°C

Инструкции по впрыску
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.03%, otherwise porosity and surface defects (e.g. smearing) may occur. Predrying is recommended even when sealed original containers are being used. To avoid internal stresses, a low shear load should be used for processing. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. High-temperature polymers place increased demands on the tool steels employed. Please contact us for further information.

Инструкции по впрыску

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.03%, otherwise porosity and surface defects (e.g. smearing) may occur. Predrying is recommended even when sealed original containers are being used. To avoid internal stresses, a low shear load should be used for processing. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. High-temperature polymers place increased demands on the tool steels employed. Please contact us for further information.

Примечание
1 .	Not recognized by UL.

Тип материала	Категория	Производитель
ULTEM™ 1010M resin	PEI	SABIC Innovative Plastics
Pyramid™ II220 (Compression Molded)	PEI	Polymics, Ltd.
ULTEM™ HU2110 resin	PEI	SABIC Innovative Plastics
EnCom PEI 0901	PEI	EnCom, Inc.
LNP™ THERMOCOMP™ EC006PXQ compound	PEI	SABIC Innovative Plastics
ULTEM™ 2200R resin	PEI	SABIC Innovative Plastics