Описание материалов:
Lustran ABS LGM is a low-gloss, easy-flow grade of ABS (Acrylonitrile Butadiene Styrene). This general-purpose injection molding grade offers an excellent balance of rigidity, impact strength, and abuse resistance.
Lustran ABS LGM resin is designed for applications requiring stringent physical properties and a high-tech, low-gloss appearance. Typical applications include power tool housings; lawn and garden equipment; telecommunications equipment; and business machine applications, such as keyboard housings, keypads, and keycaps. As with any product, use of Lustran ABS LGM resin in a given application must be tested (including but not limited to field testing) in advance by the user to determine suitability.
| Главная Информация | |
|---|
| Характеристики | - Жесткий, высокий
- Глянец, низкий
- Хорошая ударопрочность
- Хорошая мобильность
- Универсальный
|
| Используется | - Оборудование для газонов и сада
- Электропитание/другие инструменты
- Бизнес-оборудование
- Коммуникационное оборудование
- Чехол
|
| Рейтинг агентства | |
| Формы | |
| Метод обработки | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 1.05 | g/cm³ | ASTM D792 |
| Удельный объем | 0.950 | cm³/g | ASTM D792 |
| Массовый расход расплава (MFR) | | | ASTM D1238 |
| 220°C/10.0 kg | 21 | g/10 min | ASTM D1238 |
| 230°C/3.8 kg | 7.0 | g/10 min | ASTM D1238 |
| Формовочная усадка-
Поток | 0.40 - 0.70 | % | ASTM D955 |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость Роквелла (R-Scale) | 105 | | ASTM D785 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Модуль растяжения | 2210 | MPa | ASTM D638 |
| Прочность на растяжение (Yield) | 35.9 | MPa | ASTM D638 |
| Флекторный модуль | 2480 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 72.4 | MPa | ASTM D790 |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Зубчатый изод Impact (23°C, 3.18 mm) | 170 | J/m | ASTM D256 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Температура отклонения при нагрузке | | | ASTM D648 |
| 0.45 MPa, unannealed, 3.18mm | 88.9 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 12.7mm | 92.2 | °C | ASTM D648 |
| 0.45 MPa, annealed, 3.18mm | 100 | °C | ASTM D648 |
| 0.45 MPa, annealed, 12.7mm | 102 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.18mm | 75.6 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 12.7mm | 87.2 | °C | ASTM D648 |
| 1.8 MPa, annealed, 3.18mm | 95.0 | °C | ASTM D648 |
| 1.8 MPa, annealed, 12.7mm | 100 | °C | ASTM D648 |
| Викат Температура размягчения | 106 | °C | ASTM D1525 1 |
| CLTE-
Поток (-30 to 30°C) | 9.0E-5 | cm/cm/°C | ASTM D696 |
| RTI Elec (1.57 mm) | 60.0 | °C | UL 746 |
| RTI Imp (1.57 mm) | 60.0 | °C | UL 746 |
| RTI Str (1.57 mm) | 60.0 | °C | UL 746 |
| Воспламеняемость | Номинальное значение | | Метод испытания |
|---|
| Огнестойкость | | | UL 94 |
| 1.57 mm | HB | | UL 94 |
| 3.18 mm | HB | | UL 94 |
| Инъекция | Номинальное значение | Единица измерения | |
|---|
| Температура сушки | | | |
| A | 82.2 - 87.8 | °C | |
| B | 71.1 - 76.7 | °C | |
| Время сушки | | | |
| A | 2.0 | hr | |
| B | 4.0 | hr | |
| Рекомендуемая максимальная влажность | < 0.10 | % | |
| Рекомендуемый размер снимка | 50 - 75 | % | |
| Рекомендуемый Макс измельчения | 20 | % | |
| Задняя температура | 235 - 249 | °C | |
| Средняя температура | 241 - 254 | °C | |
| Передняя температура | 246 - 260 | °C | |
| Температура сопла | 246 - 260 | °C | |
| Температура обработки (расплава) | 246 - 266 | °C | |
| Температура формы | 43.3 - 65.6 | °C | |
| Давление впрыска | 68.9 - 110 | MPa | |
| Скорость впрыска | Fast | | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Тонаж зажима | 2.8 - 5.5 | kN/cm² | |
| Подушка | < 6.35 | mm | |
| Отношение винта L/D | 20.0:1.0 | | |
| Коэффициент сжатия винта | 2.5:1.0 | | |
| Инструкции по впрыску |
|---|
| Hold Pressure: 50 - 75% of Injection PressureScrew Speed: Moderate |
| Примечание |
|---|
| 1 . | 标准 B (120°C/h) |