CYCOM® 890 RTM
| Категория | Epoxy, Epoxy; Epoxide |
| Производитель | Cytec Industries Inc. |
| Торговая марка | CYCOM® |
| Порт | Китай Шанхайский порт |
| Торговые условия | FOB, CFR, CIF |
| Платежное средство | L/C, T/T, Western Union |
YVyEnE_CYCOM-890-RTM.pdf  |
|
| Контактная информация |  Служба поддержки клиентов Вичат |
|
|
|
Описание материалов:
CYCOM® 890 RTM is a one-part liquid epoxy resin system. It has one month out-life at room temperature which reduces the time required for the freeze-thaw-storage processes in a production environment. Its frozen storage shelf-life is 12 months at -18°C (0°F).
CYCOM 890 RTM's viscosity is low enough at 80°C (175°F) to allow injection without excessive heating of either the resin or the transfer pipework. When the resin is heated to cure temperature its viscosity is further reduced, helping to ensure full wet-out of the reinforcing fibers. CYCOM 890 RTM is fully cured after two hours at 180°C (355°F) after which it will have a continuous dry service performance of 170°C (338°F) and a continuous hot/wet service performance of 160°C (320°F)
If needed, an optional free-standing postcure for two hours at 200°C (390°F) can be used. After postcure the resin will have a continuous dry service performance of 195°C (383°F) and a continuous hot/wet service performance of 170°C (338°F). CYCOM 890 RTM is compatible with the range of reinforcing fibers used in manufacturing composite components, i.e., carbon, glass, aramid, etc.
A fully compatible binder system, CYCOM® 7720 has been developed for use with CYCOM 890 RTM. The binder is available pre-coated onto fabric. A separate datasheet for CYCOM 7720 is available on request.
CYCOM 890 RTM's viscosity is low enough at 80°C (175°F) to allow injection without excessive heating of either the resin or the transfer pipework. When the resin is heated to cure temperature its viscosity is further reduced, helping to ensure full wet-out of the reinforcing fibers. CYCOM 890 RTM is fully cured after two hours at 180°C (355°F) after which it will have a continuous dry service performance of 170°C (338°F) and a continuous hot/wet service performance of 160°C (320°F)
If needed, an optional free-standing postcure for two hours at 200°C (390°F) can be used. After postcure the resin will have a continuous dry service performance of 195°C (383°F) and a continuous hot/wet service performance of 170°C (338°F). CYCOM 890 RTM is compatible with the range of reinforcing fibers used in manufacturing composite components, i.e., carbon, glass, aramid, etc.
A fully compatible binder system, CYCOM® 7720 has been developed for use with CYCOM 890 RTM. The binder is available pre-coated onto fabric. A separate datasheet for CYCOM 7720 is available on request.
| Главная Информация | |
|---|---|
| Характеристики |
|
| Используется |
|
| Формы |
|
| Физический | Номинальное значение | Единица измерения | |
|---|---|---|---|
| Удельный вес 1 | 1.22 | g/cm³ |
| Механические | Номинальное значение | Единица измерения | |
|---|---|---|---|
| Модуль растяжения 2(24°C) | 3030 | MPa | |
| Прочность на растяжение 3(24°C) | 68.9 | MPa | |
| Удлинение при растяжении 4(Break) | 6.3 | % | |
| Флекторный модуль 5 | 3130 | MPa | |
| Flexural Strength 6 | 136 | MPa | |
| Модуль сдвига 7 | 1170 | MPa |
| Примечание | |
|---|---|
| 1 . | Neat Resin |
| 2 . | Neat Resin |
| 3 . | Neat Resin |
| 4 . | Neat Resin |
| 5 . | Neat Resin |
| 6 . | Neat Resin |
| 7 . | Neat Resin, 180°F |
| Тип материала | Категория | Производитель |
|---|---|---|
| Epic Epoxy S7403 | Epoxy | Epic Resins |
| SHIN-A SEV-3409 | Epoxy | SHIN-A T&C |
| Ablebond 967-3 | Epoxy | Henkel Ablestik |
| BJB Epoxy TC-1614 A/B | Epoxy | BJB Enterprises, Inc. |
| Devcon Plastic Welder™ | Epoxy | Devcon |
| EPO-TEK® H70E-2 | Epoxy | Epoxy Technology Inc. |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved