LUVOCOM® 20/SCF/30

Категория PPA, Polyphthalamide
Производитель Lehmann & Voss & Co.
Торговая марка LUVOCOM®
Порт Китай Шанхайский порт
Торговые условия FOB, CFR, CIF
Платежное средство L/C, T/T, Western Union
PDF XUmpgL_LUVOCOM-20-SCF-30.pdf
Контактная информация
EMAIL US sales@su-jiao.com

Служба поддержки клиентов Вичат
Описание материалов:
LUVOCOM®20/SCF/30 is a polyxylene amide (PPA) material, and the filler is 30% carbon fiber reinforced material. This product is available in Europe,.

LUVOCOM®The main features of 20/SCF/30 are:
  • Conductivity
  • High stiffness
  • high strength
  • Electrostatic protection

Typical application areas include:
  • engineering/industrial accessories
  • Electrical/electronic applications
  • textile/fiber
  • Automotive Industry
  • business/office supplies
Главная Информация
Наполнитель/армирование
  • Армированный углеродным волокном материал, 30% наполнитель по весу
Характеристики
  • Проводящий
  • Жесткий, высокий
  • Высокая прочность
  • Защита от электростатического разряда
Используется
  • Шестерня
  • Текстильные изделия
  • Инженерные аксессуары
  • Переключатель
  • Применение в автомобильной области
  • Бизнес-оборудование
  • Подшипник
Внешний вид
  • Натуральный цвет
ФизическийНоминальное значениеЕдиница измеренияМетод испытания
Плотность 1.31g/cm³ISO 1183
Формовочная усадка 0.0 - 0.10%DIN 16901
Поглощение воды (23°C, 24 hr)< 0.30%
МеханическиеНоминальное значениеЕдиница измеренияМетод испытания
Модуль растяжения 31000MPaISO 527-2
Tensile Stress (Break)365MPaISO 527-2
Растяжимое напряжение (Yield)1.8%ISO 527-2
Флекторный модуль 27000MPaISO 178
Флекторный стресс 500MPaISO 178
Flexural Strain at Flexural Strength 2.3%ISO 178
ТепловойНоминальное значениеЕдиница измеренияМетод испытания
Максимальная рабочая температура- Короткий срок 195°C
ЭлектрическийНоминальное значениеЕдиница измеренияМетод испытания
Insulation Resistance ohmsIEC 60167
ВоздействиеНоминальное значениеЕдиница измеренияМетод испытания
Ударная прочность (23°C)9.0kJ/m²ISO 179/1eA
Charpy Unnotched Impact Strength (23°C)75kJ/m²ISO 179/1eU
ТепловойНоминальное значениеЕдиница измеренияМетод испытания
Heat Deflection Temperature (1.8 MPa, Unannealed)270°CISO 75-2/A
Температура непрерывного использования 165°CUL 746B
ЭлектрическийНоминальное значениеЕдиница измеренияМетод испытания
Удельное сопротивление поверхности < 1.0E+5ohmsIEC 60093
ИнъекцияНоминальное значениеЕдиница измерения
Температура сушки
    A 80.0°C
    Vacuum dryer, B 105°C
Время сушки
    A 16hr
    Vacuum dryer, B 4.0 - 5.0hr
Рекомендуемая максимальная влажность 0.050%
Задняя температура 320 - 340°C
Средняя температура 320 - 345°C
Передняя температура 325 - 350°C
Температура сопла 320 - 330°C
Температура обработки (расплава) 330°C
Температура формы 135 - 160°C
Инструкции по впрыску
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.05%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. As the material absorbs water rapidly, originally sealed containers should only be opened immediately before processing. Processing temperatures above 340°C may very rapidly cause thermal damage and should therefore be avoided. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. High-temperature polymers place increased demands on the tool steels employed. Please contact us for further information.
Тип материала Категория Производитель
LUVOCOM® 20-8637 PPA LEHVOSS Group
INLUBE PPAGF20TF15 PPA Infinity LTL Engineered Compounds
LNP™ THERMOCOMP™ UF0033 compound PPA SABIC Innovative Plastics Europe
RTP 4007 HI PPA RTP Company
LUVOCOM® 20/XCF/30 PPA Lehmann & Voss & Co.
OnForce™ LFT AM-60LGF/001 BLACK PPA PolyOne Corporation
Получите информацию об этом продукте следующим способом.
Телефон+086 13424755533
EMAIL US sales@su-jiao.com

Служба поддержки клиентов Вичат
Copyright © russianpolymer.com All Rights Reserved