Описание материалов:
Menzolit® HPC 1300 is a sheet moulding compound based on unsaturated polyester resin. The product is glass fibre reinforced and contains mineral fillers. In case of fire the product doesn't melt, neither does it form droplets nor is smoke generation excessive. The material is compression moulded in heated steel moulds. It is recommended to work with chrome plated tools. The product contains no halogens.
Menzolit® HPC 1300 is a special SMC for high strength applications. The glass level has been selected to combine mouldability with high strength and stiffness properties in orientation direction. The reinforcement is composed of chopped, randomly distributed glass fibers and additional unchopped, continuous and lengthwise oriented glass fibers. This leads to very high stiffness and strength properties along with the unidirectional fibers. The flowabilty in orientation direction is reduced. This orientation influences flow during moulding and the anisotropic material properties have to be kept in mind during part design and part moulding. Typical applications are load bearing components, for instance bumpers and power train substructures.
| Главная Информация | |
|---|
| Наполнитель/армирование | - Стекло \ Mineral, 50% наполнитель по весу
|
| Характеристики | - Огнестойкий
- Хорошая плавность
- Хорошая жесткость
- Без галогенов
- Высокая термостойкость
- Высокая прочность
- Низкий уровень дыма
|
| Используется | |
| Внешний вид | |
| Формы | - Smc-лист формовочный состав
|
| Метод обработки | |
| Код маркировки деталей (ISO 11469) | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Плотность | 1.70 | g/cm³ | ISO 1183 |
| Формовочная усадка | | | |
| -- 1 | 0.0 | % | DIN 53464 |
| -- | -0.030 | % | ISO 2577 |
| Поглощение воды (Saturation, 23°C) | < 0.50 | % | ISO 62 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Модуль растяжения (Compression Molded) | 25000 | MPa | ISO 527-2 |
| Tensile Stress (Yield, Compression Molded) | 415 | MPa | ISO 527-2 |
| Растяжимое напряжение (Break, Compression Molded) | 1.6 | % | ISO 527-2 |
| Флекторный модуль (Compression Molded) | 28000 | MPa | ISO 178 |
| Флекторный стресс (Compression Molded) | 743 | MPa | ISO 178 |
| Сжимающее напряжение | 370 | MPa | ISO 14126 |
| Poisson's Ratio | 0.14 | | Internal Method |
| Matrix Crazing Strain | 0.50 | % | Internal Method |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Ударная прочность (Compression Molded) | 370 | kJ/m² | ISO 179 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | > 200 | °C | ISO 75-2/A |
| Температура непрерывного использования | 170 | °C | Internal Method |
| Температура перехода стекла | 162 | °C | DSC |
| CLTE-
Поток | 7.0E-6 | cm/cm/°C | ISO 11359-2 |
| Воспламеняемость | Номинальное значение | | Метод испытания |
|---|
| Огнестойкость (3.00 mm) | HB | | UL 94 |
| Инъекция | Номинальное значение | Единица измерения | |
|---|
| Температура формы | 140 to 160 | °C | |
| Давление впрыска | 8.00 to 10.0 | MPa | |
| Примечание |
|---|
| 1 . | Post Molding Shrinkage |