Описание материалов:
Lustran ABS 248FC resin is a high-gloss, medium-impact grade of ABS (acrylonitrile butadiene styrene). This injection molding grade offers a good balance of physical properties and has been designed to be compliant with both medical and food contact regulations.
Lustran ABS 248FC resin is used in applications requiring rigidity and intermediate abuse resistance. As with any product, use of Lustran ABS 248FC resin in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability.
Lustran ABS 248FC 000000 (natural) complies with FDA regulation 21 CFR 181.32 for repeated-use food-contact applications. It is also compliant with EU Directive 2002/72/EC and its amendments (2004/1/EC, 2004/19/EC, 2005/79/EC, 2008/39/EC) relating to plastic materials and articles intended to come into contact with foodstuffs.
Lustran ABS 248FC resin is designated as "medical-grade" and has met the requirements of the USP Class VI and ISO 10993, Part I "Biological Evaluation of Medical Devices" tests with human tissue contact time of 30 days or less. Only medical-grade resins may be considered as candidates for applications requiring biocompatibility. . Regrind must not be used in medical applications requiring biocompatibility.
| Главная Информация | |
|---|
| Характеристики | - Радиационная дезинфекция
- Подсветка
- Дезинфекция оксида этилена
- Биологическая Совместимость
- Соответствие пищевого контакта
- Средняя ударопрочность
|
| Используется | - Неспецифическое применение пищи
- Медицинские принадлежности/принадлежности для ухода
|
| Рейтинг агентства | - EC 1907/2006 (REACH)
- ЕС 2004/19/ЕС
- Управление по санитарному надзору за качеством пищевых продуктов и медикаментов 21 CFR 181,32
- ISO 10993-часть I
- USP категория VI
- Европа 2002/72/EC
|
| Формы | |
| Метод обработки | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 1.06 | g/cm³ | ASTM D792 |
| Удельный объем | 0.940 | cm³/g | ASTM D792 |
| Массовый расход расплава (MFR) (230°C/3.8 kg) | 5.0 | g/10 min | ASTM D1238 |
| Формовочная усадка-
Поток | 0.40 - 0.60 | % | ASTM D955 |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость Роквелла (R-Scale) | 112 | | ASTM D785 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Модуль растяжения | 2620 | MPa | ASTM D638 |
| Прочность на растяжение (Yield) | 46.9 | MPa | ASTM D638 |
| Флекторный модуль | 2690 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 73.8 | MPa | ASTM D790 |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Зубчатый изод Impact | | | ASTM D256 |
| -40°C, 3.18 mm | 48 | J/m | ASTM D256 |
| 23°C, 3.18 mm | 220 | J/m | ASTM D256 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Температура отклонения при нагрузке | | | ASTM D648 |
| 0.45 MPa, unannealed, 12.7mm | 93.3 | °C | ASTM D648 |
| 0.45 MPa, annealed, 12.7mm | 100 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 12.7mm | 86.1 | °C | ASTM D648 |
| 1.8 MPa, annealed, 12.7mm, molded | 102 | °C | ASTM D648 |
| 1.8 MPa, annealed, 12.7mm | 95.6 | °C | ASTM D648 |
| Викат Температура размягчения | 80.0 | °C | ASTM D1525 1 |
| CLTE-
Поток (-30 to 30°C) | 8.1E-5 | cm/cm/°C | ASTM D696 |
| Инъекция | Номинальное значение | Единица измерения | |
|---|
| Температура сушки | 82.2 - 87.8 | °C | |
| Время сушки | 2.0 | hr | |
| Рекомендуемая максимальная влажность | < 0.10 | % | |
| Рекомендуемый размер снимка | 50 - 75 | % | |
| Задняя температура | 235 - 249 | °C | |
| Средняя температура | 241 - 254 | °C | |
| Передняя температура | 246 - 260 | °C | |
| Температура сопла | 246 - 260 | °C | |
| Температура обработки (расплава) | 246 - 266 | °C | |
| Температура формы | 43.3 - 65.6 | °C | |
| Давление впрыска | 68.9 - 110 | MPa | |
| Скорость впрыска | Fast | | |
| Back Pressure | 0.00 - 0.172 | MPa | |
| Тонаж зажима | 2.8 - 5.5 | kN/cm² | |
| Подушка | < 6.35 | mm | |
| Отношение винта L/D | 20.0:1.0 | | |
| Коэффициент сжатия винта | 2.5:1.0 | | |
| Инструкции по впрыску |
|---|
| Hold Pressure: 50 to 75% of Injection PressureScrew Speed: ModerateDrying at 160°-170°F for 4 hours is also adequate. |
| Примечание |
|---|
| 1 . | 标准 B (120°C/h) |