TUFLIN™ HS-7029 NT 7
| Категория | LLDPE, Linear Low Density Polyethylene Resin |
| Производитель | The Dow Chemical Company |
| Торговая марка | TUFLIN™ |
| Порт | Китай Шанхайский порт |
| Торговые условия | FOB, CFR, CIF |
| Платежное средство | L/C, T/T, Western Union |
UbExS7_TUFLIN-HS-7029-NT-7.pdf  |
|
| Контактная информация |  Служба поддержки клиентов Вичат |
|
|
|
Описание материалов:
TUFLIN™ HS-7029 NT 7 Linear Low Density Polyethylene Resin is an ethylene-hexene copolymer designed for cast and blown film applications such as trash bags, industrial can liners, heavy duty shipping sacks and retail bags. Films extruded with HS-7029 exhibit superb toughness, high tensile strength and elongation, excellent tear and puncture resistance, and are readily heat sealable.
Applications: Trash bags, industrial can liners, heavy duty shipping sacks and retail bags
Complies with:
Applications: Trash bags, industrial can liners, heavy duty shipping sacks and retail bags
Complies with:
- U.S. FDA 21 CFR 177.1520(c)3.1a (with Restrictions)
- Consult the regulations for complete details
| Главная Информация | |
|---|---|
| Добавка |
|
| Рейтинг агентства |
|
| Формы |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Удельный вес | 0.918 | g/cm³ | ASTM D792 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 1.3 | g/10 min | ASTM D1238 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Толщина пленки протестирована | 25 | µm | Internal method |
| Энергия прокола пленки | 3.39 | J | Internal method |
| Сила прокола пленки | 44.5 | N | Internal method |
| Сопротивление проколу пленки | 18.6 | J/cm³ | Internal method |
| Прочность пленки | ASTM D882 | ||
| MD | 82.7 | J/cm³ | ASTM D882 |
| TD | 91.0 | J/cm³ | ASTM D882 |
| Сектантный модуль | ASTM D882 | ||
| 1% secant, MD | 221 | MPa | ASTM D882 |
| 2% secant, MD | 200 | MPa | ASTM D882 |
| 1% secant, TD | 303 | MPa | ASTM D882 |
| 2% secant, TD | 255 | MPa | ASTM D882 |
| Прочность на растяжение | ASTM D882 | ||
| MD : Yield | 10.3 | MPa | ASTM D882 |
| TD : Yield | 11.7 | MPa | ASTM D882 |
| MD : Fracture | 33.8 | MPa | ASTM D882 |
| TD : Fracture | 29.6 | MPa | ASTM D882 |
| Удлинение при растяжении | ASTM D882 | ||
| MD : Fracture | 500 | % | ASTM D882 |
| TD : Fracture | 600 | % | ASTM D882 |
| Ударное падение Dart | 160 | g | ASTM D1709A |
| Elmendorf Tear Strength 1 | ASTM D1922 | ||
| MD | 350 | g | ASTM D1922 |
| TD | 600 | g | ASTM D1922 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Викат Температура размягчения | 99.0 | °C | ASTM D1525 |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Блеск (45°) | 22 | ASTM D2457 | |
| Haze | 28 | % | ASTM D1003 |
| Инструкции по экструзии |
|---|
| Fabrication Conditions for 1 mil monolayer blown film at 100% Die Diameter: 8 in. Screw Type: DSB II Die Gap: 70 mil Melt Temperature: 405 °F Output: 12 lb/hr/in. of die circumference Screw Size: 3.5 in. Blow-Up Ratio: 2.5 to 1 Screw Speed: 39 rpm Frost Line Height: 52 in. |
| Примечание | |
|---|---|
| 1 . | Method B |
| Тип материала | Категория | Производитель |
|---|---|---|
| Arak LLDPE LL0220AA | LLDPE | Shazand (Arak) Petrochemical Corporation |
| ASI POLYETHYLENE CP 878-01 Natural | LLDPE | A. Schulman Inc. |
| Formolene® L62009H | LLDPE | Formosa Plastics Corporation, U.S.A. |
| Hanwha Total PE 4142W | LLDPE | HANWHA TOTAL PETROCHEMICALS Co., Ltd. |
| Lotrène® LLDPE Q1018M | LLDPE | QATOFIN Company Limited |
| ADVANCENE™ EE-1801-AAB | LLDPE | ETHYDCO |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved