Riblene® FL 23 I
| Категория | LDPE, Low Density Polyethylene |
| Производитель | Versalis S.p.A. |
| Торговая марка | Riblene® |
| Порт | Китай Шанхайский порт |
| Торговые условия | FOB, CFR, CIF |
| Платежное средство | L/C, T/T, Western Union |
U7QWX5_RibleneFL23I.pdf  |
|
| Контактная информация |  Служба поддержки клиентов Вичат |
|
|
|
Описание материалов:
Riblene FL 23 I is a low density polyethylene (LDPE) additivated with slip agent, ideal for blown film extrusion.
Riblene FL 23 I is characterised by a good balance between proc-essability and mechanical properties.
Films manufactured with Riblene FL 23 I are easily heat shrinkable and characterised by good optical and mechanical properties.
Main Applications
Riblene FL 23 I is recommended for general blown film applications, for the production of low gauge film and shrink film, for lamination and for blending.
Riblene FL 23 I is characterised by a good balance between proc-essability and mechanical properties.
Films manufactured with Riblene FL 23 I are easily heat shrinkable and characterised by good optical and mechanical properties.
Main Applications
Riblene FL 23 I is recommended for general blown film applications, for the production of low gauge film and shrink film, for lamination and for blending.
| Главная Информация | |
|---|---|
| Добавка |
|
| Характеристики |
|
| Используется |
|
| Рейтинг агентства |
|
| Формы |
|
| Метод обработки |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Плотность | 0.923 | g/cm³ | ISO 1183 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 2.2 | g/10 min | ISO 1133 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Коэффициент трения (vs. Itself - Dynamic, Blown Film) | 0.13 | ISO 8295 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Толщина пленки протестирована | 40 | µm | |
| Толщина пленки-рекомендовано/доступно | 25 to 80 µm | ||
| Модуль растяжения | ISO 527-3 | ||
| 1% secant, MD : 40 µm, blown film | 180 | MPa | ISO 527-3 |
| 1% secant, TD : 40 µm, blown film | 190 | MPa | ISO 527-3 |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 40 µm, blown film | 11.0 | MPa | ISO 527-3 |
| TD : Yield, 40 µm, blown film | 11.0 | MPa | ISO 527-3 |
| MD : Broken, 40 µm, blown film | 25.0 | MPa | ISO 527-3 |
| TD : Broken, 40 µm, blown film | 22.0 | MPa | ISO 527-3 |
| Удлинение при растяжении | ISO 527-3 | ||
| MD : Broken, 40 µm, blown film | 300 | % | ISO 527-3 |
| TD : Broken, 40 µm, blown film | 650 | % | ISO 527-3 |
| Ударное падение Dart 1(40 µm, Blown Film) | 130 | g | ISO 7765-1 |
| Elmendorf Tear Strength 2 | ISO 6383-2 | ||
| MD : 40.0 µm | 80.0 | kN/m | ISO 6383-2 |
| TD : 40.0 µm | 55.0 | kN/m | ISO 6383-2 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Температура ломкости | < -75.0 | °C | ASTM D746 |
| Викат Температура размягчения | 93.0 | °C | ISO 306/A |
| Температура плавления | 113 | °C | Internal method |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Блеск (45°, 40.0 µm, Blown Film) | 72 | ASTM D2457 | |
| Haze (40.0 µm, Blown Film) | 5.5 | % | ISO 14782 |
| Экструзия | Номинальное значение | Единица измерения | |
|---|---|---|---|
| Температура расплава | 160 - 190 | °C |
| Примечание | |
|---|---|
| 1 . | F50 |
| 2 . | Blown Film |
| Тип материала | Категория | Производитель |
|---|---|---|
| Maxxam™ FR PE 112 Natural RoHS | LDPE | PolyOne Corporation |
| Prixene® EB450I18 | LDPE | POLYMAT |
| SABIC® LDPE Powder 1922P3 | LDPE | Saudi Basic Industries Corporation (SABIC) |
| Sinpolene MBB2672 | LDPE | Teknor Apex Asia Pacific PTE. LTD. |
| Sinpolene MBB1402 | LDPE | Teknor Apex Asia Pacific PTE. LTD. |
| Kemcor LD 0231 | LDPE | Qenos Pty Ltd |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved