Riblene® AB 10
| Категория | LDPE, Low Density Polyethylene |
| Производитель | Versalis S.p.A. |
| Торговая марка | Riblene® |
| Порт | Китай Шанхайский порт |
| Торговые условия | FOB, CFR, CIF |
| Платежное средство | L/C, T/T, Western Union |
Ai4leR_RibleneAB10.pdf  |
|
| Контактная информация |  Служба поддержки клиентов Вичат |
|
|
|
Описание материалов:
Riblene AB 10 is a high molecular weight low density polyethylene resin (LDPE) suitable for blown film extrusion.
Riblene AB 10 is characterized by a high melt strength leading to a good bubble stability during extrusion.
Films manufactured by Riblene AB 10 are easily heat shrinkable and characterized by optimum mechanical properties.
Main Applications
Riblene AB 10 is recommended for the production of greenhouse film, heavy duty shrink film and industrial bags.
Riblene AB 10 is characterized by a high melt strength leading to a good bubble stability during extrusion.
Films manufactured by Riblene AB 10 are easily heat shrinkable and characterized by optimum mechanical properties.
Main Applications
Riblene AB 10 is recommended for the production of greenhouse film, heavy duty shrink film and industrial bags.
| Главная Информация | |
|---|---|
| Характеристики |
|
| Используется |
|
| Рейтинг агентства |
|
| Формы |
|
| Метод обработки |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Плотность | 0.918 | g/cm³ | ISO 1183 |
| Массовый расход расплава (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 0.15 | g/10 min | ISO 1133 |
| 190°C/5.0 kg | 0.60 | g/10 min | ISO 1133 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Коэффициент трения (Dynamic, Blown Film) | > 0.50 | ASTM D1894 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Толщина пленки протестирована | 70 | µm | |
| Толщина пленки-рекомендовано/доступно | 60 to 250 µm | ||
| Модуль растяжения | ISO 527-3 | ||
| 1% sectioning, MD : 70 µm | 150 | MPa | ISO 527-3 |
| 1% sectioning, TD : 70 µm, blown film | 180 | MPa | ISO 527-3 |
| Tensile Stress | ISO 527-3 | ||
| MD : yield, 70 µm, blow film | 9.00 | MPa | ISO 527-3 |
| TD : yield, 70 µm, blow film | 9.00 | MPa | ISO 527-3 |
| MD : broken, 70 µm, blown film | 27.0 | MPa | ISO 527-3 |
| TD : broken, 70 µm, blown film | 25.0 | MPa | ISO 527-3 |
| Удлинение при растяжении | ISO 527-3 | ||
| MD : broken, 70 µm, blown film | 400 | % | ISO 527-3 |
| TD : broken, 70 µm, blown film | 600 | % | ISO 527-3 |
| Ударное падение Dart (70 µm, Blown Film) | 380 | g | ISO 7765-1/A |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD : 70 µm, blown film | 25 | N | ISO 6383-2 |
| TD : 70 µm, blown film | 35 | N | ISO 6383-2 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Температура ломкости | < -75.0 | °C | ASTM D746 |
| Викат Температура размягчения | 91.0 | °C | ISO 306/A |
| Температура плавления | 109 | °C |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Блеск (45°, 70.0 µm, Blown Film) | 50 | ASTM D2457 | |
| Haze (70.0 µm, Blown Film) | 12 | % | ISO 14782 |
| Экструзия | Номинальное значение | Единица измерения | |
|---|---|---|---|
| Температура расплава | 180 - 220 | °C |
| Тип материала | Категория | Производитель |
|---|---|---|
| Sinpolene MBW014LE | LDPE | Teknor Apex Asia Pacific PTE. LTD. |
| Yanshan PE LD361 | LDPE | SINOPEC Beijing Yanshan Petrochemical |
| Bormed™ LE6609-PH | LDPE | Borealis AG |
| ExxonMobil™ LDPE LD 157CW Wire & Cable | LDPE | ExxonMobil Chemical |
| Hypel® PELD20/.920 | LDPE | Entec Polymers |
| Petrothene® NA324244 | LDPE | LyondellBasell Industries |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved