Описание материалов:
AGILITY™ 1002 Performance LDPE is a high pressure LDPE resin designed specifically to run at faster output rates on blown film lines in blends with LLDPE resins while maintaining bubble stability. This resin includes 2,000 ppm of anti-block to minimize blocking issues.
Main Characteristics:
Complies with:
Main Characteristics:
- Faster processing LDPE resin
- Designed for higher output rates in blends with LLDPE resins at 10-20% loading - - Optimized molecular structure gives improved optics in blends with LLDPE resins
Complies with:
- EU No 10/2011
- U.S.FDA 21 CFR 177.1520 (c) 2.2
- Canadian HPFB No Objection
| Главная Информация | |
|---|---|
| Добавка |
|
| Рейтинг агентства |
|
| Формы |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Удельный вес | 0.921 | g/cm³ | ASTM D792 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 0.65 | g/10 min | ASTM D1238 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Толщина пленки протестирована | 25 | µm | |
| Энергия прокола пленки | 0.565 | J | |
| Сила прокола пленки | 22.2 | N | |
| Сопротивление проколу пленки | 2.48 | J/cm³ | Internal method |
| Прочность пленки | ASTM D882 | ||
| MD | 26.5 | J/cm³ | ASTM D882 |
| TD | 51.3 | J/cm³ | ASTM D882 |
| Сектантный модуль | ASTM D882 | ||
| 1% secant, MD | 243 | MPa | ASTM D882 |
| 2% secant, MD | 221 | MPa | ASTM D882 |
| 1% secant, TD | 301 | MPa | ASTM D882 |
| 2% secant, TD | 255 | MPa | ASTM D882 |
| Прочность на растяжение | ASTM D882 | ||
| MD : Yield | 28.3 | MPa | ASTM D882 |
| TD : Yield | 13.0 | MPa | ASTM D882 |
| MD : Fracture | 29.6 | MPa | ASTM D882 |
| TD : Fracture | 16.2 | MPa | ASTM D882 |
| Удлинение при растяжении | ASTM D882 | ||
| MD : Fracture | 110 | % | ASTM D882 |
| TD : Fracture | 430 | % | ASTM D882 |
| Ударное падение Dart | 75 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD | 290 | g | ASTM D1922 |
| TD | 95 | g | ASTM D1922 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Викат Температура размягчения | 94.0 | °C | ASTM D1525 |
| Температура плавления (DSC) | 109 | °C | Internal method |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Блеск (45°) | 51 | ASTM D2457 | |
| Haze | 10 | % | ASTM D1003 |
| Инструкции по экструзии |
|---|
| Fabrication Conditions For Blown Film: Screw Type: DSB II Die Gap: 70 mil Melt Temperature: 398°F Output: 12 lb/hr/in. of die circumference Screw size: 3.5 in. Die Diameter: 8 in. Blow-Up Ratio: 2.5 to 1 Screw Speed: 55 rpm Frost Line Height: 37 in. |
| Тип материала | Категория | Производитель |
|---|---|---|
| ICORENE® N2101 | LDPE | ICO Polymers EMEA, A Division of A. Schulman |
| Kazan LDPE 16813-070 OKP 22 111 4102 | LDPE | Kazanorgsintez Joint Stock Company |
| PAXOTHENE® NA112-27 | LDPE | USI Corporation |
| Petrothene® NA951000 | LDPE | LyondellBasell Industries |
| MarFlex® 5429 | LDPE | Chevron Phillips Chemical Company LLC |
| MARPOL® LDM 733 | LDPE | Marco Polo International, Inc. |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved