DOW™ LDPE 312E

Категория	LDPE, Low Density Polyethylene Resin
Производитель	The Dow Chemical Company
Торговая марка	DOW™ LDPE
Порт	Китай Шанхайский порт
Торговые условия	FOB, CFR, CIF
Платежное средство	L/C, T/T, Western Union
PDF	R0qvvg_DOW-LDPE-312E.pdf
Контактная информация	EMAIL US  sales@su-jiao.com Служба поддержки клиентов Вичат

Описание материалов:

DOW LDPE 312E is a low melt index, low density polyethylene resin containing slip agent and opening agent. DOW LDPE 312E has excellent processing performance and is specially developed for blown film processing production lines. The application of this product can significantly improve production capacity.

In addition, the resin also has excellent drafting properties. The resin can be used alone or blended with LLDPE resin.

Application fields:
Health and hygiene films, food packaging, cold snack shrink films, agricultural films, shopping bags, garbage bags, composite films

Main characteristics:

Excellent processability and drafting performance

The blend with LLDPE has good physical properties

It can be easily extruded using conventional blown film technology, and the melt temperature range is 160 to 195°C

DOW LDPE 312E should meet the requirements of the following regulations:

U.S. Food and Drug Administration Regulation 21 CFR 177.1520 (c) 2.2

EU, No 10/2011

Canadian HPFB No Objection

U.S. FDA-DMF

please check the regulations for complete details.

slip agent content: 385 ppm
opening agent content: 900 ppm

Главная Информация
Добавка	Антикаширующий агент (900 ppm) Агент скольжения (385 ppm)
Рейтинг агентства	DMF не Номинальная FDA 21 CFR 177,1520 (c) 2,2 HPFB (Канада) нет возражений Европа без 10/2011
Формы	Частицы

Физический	Номинальное значение	Единица измерения	Метод испытания
Удельный вес	0.923	g/cm³	ASTM D792
Массовый расход расплава (MFR) (190°C/2.16 kg)	0.75	g/10 min	ASTM D1238

Механические	Номинальное значение	Единица измерения	Метод испытания
Коэффициент трения	0.15		ASTM D1894

Пленки	Номинальное значение	Единица измерения	Метод испытания
Толщина пленки протестирована	50	µm
Энергия прокола пленки (50 µm)	1.80	J	Internal method
Сила прокола пленки (50 µm)	50.0	N	Internal method
Сопротивление проколу пленки (50 µm)	4.00	J/cm³	Internal method
Сектантный модуль			ASTM D882
2% secant, MD : 50 µm, blown film	175	MPa	ASTM D882
2% secant, TD : 50 µm, blown film	185	MPa	ASTM D882
Прочность на растяжение			ASTM D882
MD : Yield, 50 µm, blown film	11.0	MPa	ASTM D882
TD : Yield, 50 µm, blown film	11.0	MPa	ASTM D882
MD : Broken, 50 µm, blown film	25.0	MPa	ASTM D882
TD : Broken, 50 µm, blown film	23.0	MPa	ASTM D882
Удлинение при растяжении			ASTM D882
MD : Broken, 50 µm, blown film	390	%	ASTM D882
TD : Broken, 50 µm, blown film	570	%	ASTM D882
Ударное падение Dart (50 µm, Blown Film)	170	g	ASTM D1709A
Elmendorf Tear Strength			ASTM D1922
MD : 50 µm, blown film	350	g	ASTM D1922
TD : 50 µm, blown film	260	g	ASTM D1922

Оптический	Номинальное значение	Единица измерения	Метод испытания
Блеск (45°, 50.0 µm, Blown Film)	58		ASTM D2457
Haze (50.0 µm, Blown Film)	9.2	%	ASTM D1003

Экструзия	Номинальное значение	Единица измерения
Температура расплава	160 - 195	°C

Инструкции по экструзии
吹塑薄膜的制造条件：螺杆类型：通用输出：25 kg/h 模具直径：150 mm。放大比：2.5 螺杆速度：77 rpm

Тип материала	Категория	Производитель
SABIC® LDPE 2201H0W	LDPE	Saudi Basic Industries Corporation (SABIC)
MIDILENA I LDPE B21/2	LDPE	ROMPETROL PETROCHEMICALS S.R.L.
HANWHA LDPE 955	LDPE	Hanwha Chemical
Kazan LDPE 16813-070 OKP 22 111 4101	LDPE	Kazanorgsintez Joint Stock Company
Kazan LDPE 15313-003 OKP 22 1111 2001	LDPE	Kazanorgsintez Joint Stock Company
MARPOL® LDM 740	LDPE	Marco Polo International, Inc.

Получите информацию об этом продукте следующим способом.

Телефон	+086 13424755533
EMAIL US	sales@su-jiao.com
Служба поддержки клиентов Вичат

