- INTEGRAL™ 630
INTEGRAL™ 630
| Категория | PO, Polyolefin Adhesive Film , Polyolefin, Unspecified |
| Производитель | The Dow Chemical Company |
| Торговая марка | INTEGRAL™ |
| Порт | Китай Шанхайский порт |
| Торговые условия | FOB, CFR, CIF |
| Платежное средство | L/C, T/T, Western Union |
QR3uwB_INTEGRAL-630.pdf  |
|
| Контактная информация |  Служба поддержки клиентов Вичат |
|
|
|
Описание материалов:
INTEGRAL™ 630 Polyolefin Adhesive Film is a heat-activated adhesive film specifically designed for bonding to steel and flexible polyolefins.
New experimental films are continually being developed. Please discuss your particular application needs with your Dow representative.
General Characteristics:
New experimental films are continually being developed. Please discuss your particular application needs with your Dow representative.
General Characteristics:
- Heat activation Point: 215 °F (102 °C)
- Yield: 208 ft²/lb/mil (42.6 m²/kg/25 µm)
- Available colors: Blue
- Gauge range: 0.7 - 2.0 mil (18-51 µm)
- Width: 20 - 72 in. (510 - 1830 mm)
| Главная Информация | |
|---|---|
| Внешний вид |
|
| Формы |
|
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Толщина пленки протестирована | 18 | µm | ASTM D374 |
| Толщина пленки-рекомендовано/доступно | 0.7-2.0 mil (18-51 µm) | ||
| Сектантный модуль | ASTM D882 | ||
| 1% Secant, MD : 18 µm | 384 | MPa | |
| 2% Secant, MD : 18 µm | 246 | MPa | |
| 1% Secant, TD : 18 µm | 422 | MPa | |
| 2% Secant, TD : 18 µm | 259 | MPa | |
| Прочность на растяжение | ASTM D882 | ||
| MD : Yield, 18 µm | 25.9 | MPa | |
| TD : Yield, 18 µm | 16.1 | MPa | |
| MD : Break, 18 µm | 20.8 | MPa | |
| TD : Break, 18 µm | 15.5 | MPa | |
| Удлинение при растяжении | ASTM D882 | ||
| MD : Yield, 18 µm | 160 | % | |
| TD : Yield, 18 µm | 460 | % | |
| MD : Break, 18 µm | 160 | % | |
| TD : Break, 18 µm | 460 | % | |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 18 µm | 200 | g | |
| TD : 18 µm | 150 | g | |
| Выход (25.4 µm) | 42.7 | m²/kg | Internal Method |
| Тип материала | Категория | Производитель |
|---|---|---|
| PRE-ELEC® CP 1515 | Polyolefin, Unspecified | Premix Oy |
| CALP 1100G-1 | Polyolefin, Unspecified | Lion Idemitsu Composites Co., Ltd. |
| FRAGOM G/458 NAT | Polyolefin, Unspecified | Crosspolimeri S.p.A. |
| Ecobarrier® 2012 | Polyolefin, Unspecified | Noble Polymers |
| INTEGRATE™ NE542013 | Polyolefin, Unspecified | LyondellBasell Industries |
| Lucopren® 1500H | Polyolefin, Unspecified | Lucobit AG |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved