Описание материалов:
Lustran ABS 556 resin is a low-gloss, medium-impact extrusion grade of ABS (acrylonitrile butadiene styrene). It has good melt strength for extrusion and thermoforming, and can be easily coextruded. It is easy to color with ABS color concentrates. The recommended ABS substrate is Lustran ABS 752 resin.
Lustran ABS 556 resin is used for low-gloss applications, such as motor vehicle dashboards, interior panels, and trim. This includes recreational vehicles, cars, trucks, heavy trucks, construction vehicles, forklift trucks, and farm equipment. As with any product, use of Lustran ABS 556 resin in a given application must be tested (including but not limited to field testing) in advance by the user to determine suitability.
| Главная Информация | |
|---|
| Характеристики | - Глянец, низкий
- Хорошая прочность расплава
- Хорошая окраска
- Средняя ударопрочность
|
| Используется | - Применение в автомобильной области
- Автомобильные внутренние детали
- Приборная панель автомобиля
|
| Рейтинг агентства | |
| Формы | |
| Метод обработки | - Коэкструзионное формование
- Экструзионный лист
- Термоформовка
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 1.06 | g/cm³ | ASTM D792 |
| Удельный объем | 0.950 | cm³/g | ASTM D792 |
| Массовый расход расплава (MFR) (230°C/10.0 kg) | 10 | g/10 min | ASTM D1238 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Модуль растяжения | 1520 | MPa | ASTM D638 |
| Прочность на растяжение | | | ASTM D638 |
| Yield | 19.3 | MPa | ASTM D638 |
| Fracture | 22.1 | MPa | ASTM D638 |
| Флекторный модуль | 1450 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 31.0 | MPa | ASTM D790 |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Зубчатый изод Impact | | | ASTM D256 |
| -40°C, 3.18 mm | 53 | J/m | ASTM D256 |
| -18°C, 3.18 mm | 69 | J/m | ASTM D256 |
| 23°C, 3.18 mm | 110 | J/m | ASTM D256 |
| Ударное устройство для дротиков | | | ASTM D3763 |
| -34°C, Peak Energy | 14.0 | J | ASTM D3763 |
| -34°C, Total Energy | 16.0 | J | ASTM D3763 |
| -18°C, Peak Energy | 19.0 | J | ASTM D3763 |
| -18°C, Total Energy | 23.0 | J | ASTM D3763 |
| 23°C, Total Energy | 30.0 | J | ASTM D3763 |
| 23°C, Peak Energy | 26.0 | J | ASTM D3763 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Температура отклонения при нагрузке | | | ASTM D648 |
| 0.45 MPa, not annealed | 96.1 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 86.1 | °C | ASTM D648 |
| CLTE-
Поток | 9.7E-5 | cm/cm/°C | ASTM D696 |
| RTI Elec (1.47 mm) | 60.0 | °C | UL 746 |
| RTI Imp (1.47 mm) | 60.0 | °C | UL 746 |
| RTI Str (1.47 mm) | 60.0 | °C | UL 746 |
| Воспламеняемость | Номинальное значение | | Метод испытания |
|---|
| Огнестойкость (1.47 mm) | HB | | UL 94 |
| Оптический | Номинальное значение | | Метод испытания |
|---|
| Блестящий Гарднер (60°) | < 10 | | ASTM D523 |
| Экструзия | Номинальное значение | Единица измерения | |
|---|
| Температура сушки | 82.2 - 93.3 | °C | |
| Время сушки | 3.0 - 4.0 | hr | |
| Рекомендуемая максимальная влажность | < 0.030 | % | |
| Зона цилиндра 1 темп. | 216 - 2560 | °C | |
| Зона цилиндра 2 температура. | 216 - 241 | °C | |
| Зона цилиндра 3 темп. | 216 - 241 | °C | |
| Зона цилиндра 4 темп. | 216 - 241 | °C | |
| Зона цилиндра 5 темп. | 216 - 241 | °C | |
| Температура расплава | 216 - 249 | °C | |
| Температура матрицы | 210 - 241 | °C | |
| Рулон для снятия | 62.8 - 104 | °C | |
| Инструкции по экструзии |
|---|
| Compression Ratio: 2.5:1 to 2.7:1Pump Ratio: 1.5 to 2.0Max Regrind Allowed: 40% |