- Braskem PE F-2022/0
Braskem PE F-2022/0
| Категория | LDPE, Low Density Polyethylene |
| Производитель | Braskem |
| Торговая марка | Braskem PE |
| Порт | Китай Шанхайский порт |
| Торговые условия | FOB, CFR, CIF |
| Платежное средство | L/C, T/T, Western Union |
PleT5R_Braskem-PE-F-2022-0.pdf  |
|
| Контактная информация |  Служба поддержки клиентов Вичат |
|
|
|
Описание материалов:
Excellent sealing characteristics and optical properties with well balanced mechanical properties.
Application
General purpose which require no additives; shrink films for goods; flat film for diapers and injection blow molding. Recommended film thickness: 0.025-0.100mm.
Application
General purpose which require no additives; shrink films for goods; flat film for diapers and injection blow molding. Recommended film thickness: 0.025-0.100mm.
| Главная Информация | |
|---|---|
| Характеристики |
|
| Используется |
|
| Рейтинг агентства |
|
| Формы |
|
| Метод обработки |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Удельный вес | 0.922 | g/cm³ | ASTM D792 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Толщина пленки протестирована | 25 | µm | |
| Прочность на растяжение | ASTM D882 | ||
| MD : Broken, 30 µm, blown film | 40.0 | MPa | ASTM D882 |
| TD : Broken, 30 µm, blown film | 20.0 | MPa | ASTM D882 |
| Удлинение при растяжении | ASTM D882 | ||
| MD : Broken, 30 µm, blown film | 230 | % | ASTM D882 |
| TD : Broken, 30 µm, blown film | 900 | % | ASTM D882 |
| Ударное падение Dart (30 µm, Blown Film) | 70 | g | ASTM D1709A |
| Elmendorf Tear Strength - TD (30 µm, Blown Film) | 90 | g | ASTM D1922 |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Блеск (45°, 30.0 µm, Blown Film) | 93 | ASTM D2457 | |
| Haze (30.0 µm, Blown Film) | 8.0 | % | ASTM D1003 |
| Дополнительная информация |
|---|
| Film properties taken from 25µm film produced on a 40 mm extruder with BUR=2.2:1 |
| Инструкции по экструзии |
|---|
| Blow Film Extrusion Temperature profile: 120 to 170°C. Blow up ratio: 1.8 to 3.0:1 Blow Molding Temperature profile: 180 to 310°C. The optimum processing conditions will vary according to the type of equipment used and cannot be considered as performance guarantee. |
| Тип материала | Категория | Производитель |
|---|---|---|
| Prime PE LDPE 049 | LDPE | Primex Plastics Corporation |
| Yanshan PE 112A-1 | LDPE | SINOPEC Beijing Yanshan Petrochemical |
| ExxonMobil™ LDPE LD 380BA Wire & Cable | LDPE | ExxonMobil Chemical |
| INEOS LDPE 21D430 | LDPE | INEOS Olefins & Polymers Europe |
| Petrothene® NA149000 | LDPE | LyondellBasell Industries |
| TOTAL Polyethylene LDPE CD0230 | LDPE | TOTAL Refining & Chemicals |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved