Описание материалов:
Menzolit® SMC 0421 is a sheet moulding compound based on unsaturated polyester resin. The product is glass fibre reinforced and contains mineral fillers. In case of fire the product doesn't melt, neither does it form droplets nor is smoke generation excessive. The material is compression moulded in heated steel moulds. It is highly recomended to mould in chrome plated moulds. The product contains no halogens nor any heavy metals.
Menzolit® SMC 0421 is a low density premium Class-A SMC for on-line painted exterior body applications on cars. These compounds mould to light weight parts with excellent surface quality for on-line painted body panels at high paint bake temperatures (190- 200 °C). Moulded parts comply with all regulations of the automotive industry including low C-emissions. Surface defects like waviness, fibre patterns and orange peel are not existent with this product. To achieve the highest surface quality, we recommend that tool surfaces are mirror polished.
| Главная Информация | |
|---|
| Наполнитель/армирование | - Стекло \ Mineral, 38% наполнитель по весу
|
| Характеристики | - Хорошая поверхность
- Без галогенов
- Низкий уровень дыма
- Болезненный
|
| Используется | - Автомобильные Приложения
- Автомобильные внешние части
|
| Внешний вид | |
| Метод обработки | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Плотность | 1.50 | g/cm³ | ISO 1183 |
| Формовочная усадка | | | |
| -- | -0.050 | % | ISO 2577 |
| -- 1 | 0.0 | % | DIN 53464 |
| Поглощение воды (23°C, 24 hr) | < 0.50 | % | ISO 62 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Модуль растяжения | 8000 | MPa | ISO 527-4 |
| Tensile Stress (Break) | 75.0 | MPa | ISO 527-4 |
| Растяжимое напряжение (Break) | 1.3 | % | ISO 527-4 |
| Флекторный модуль | 8000 | MPa | ISO 178 |
| Флекторный стресс | 150 | MPa | ISO 14125 |
| Сжимающее напряжение | 80.0 | MPa | ISO 14126 |
| Poisson's Ratio | 0.30 | | |
| Matrix Crazing Strain | 0.40 | % | |
| Дополнительная информация | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Содержание волокна | 38 | % | ISO 1172 |
| Обозначение материала | >UP-(MD+GF+GB)70< | | EN 14598-1 |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Charpy Unnotched Impact Strength | 70 | kJ/m² | ISO 179 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | > 200 | °C | ISO 75-2/A |
| Температура непрерывного использования | 165 | °C | |
| Температура перехода стекла | 200 | °C | ISO 11357-2 |
| CLTE-
Поток | 1.0E-5 | cm/cm/°C | ISO 11359-2 |
| Воспламеняемость | Номинальное значение | | Метод испытания |
|---|
| Огнестойкость (3.00 mm) | HB | | UL 94 |
| Инъекция | Номинальное значение | Единица измерения | |
|---|
| Температура формы | 145 to 155 | °C | |
| Давление впрыска | 3.00 to 8.00 | MPa | |
| Примечание |
|---|
| 1 . | Post Molding Shrinkage |