Описание материалов:
Menzolit® BMC 2500 is a bulk moulding compound based on unsaturated polyester resin. The product is glass fibre reinforced and contains mineral fillers. In case of fire the product doesn't melt, neither does it form droplets nor is smoke generation excessive. The material is injection moulded in heated steel moulds. It is recommended to work with chrome plated tools. The product contains no halogens.
Menzolit® BMC 2500 is a special BMC for high voltage isolating applications. The glass content is set to a level that combines good mouldability with good strength and stiffness properties. The fire retardancy level HB according to the UL 94 is achieved. The electrical properties are improved to have exceptional high isolation properties. When moulding this material, a high moulding pressure is important to achieve a well densified material matrix to guarantee high voltage applications. Typical applications are isolating components in high voltage applications.
| Главная Информация | |
|---|
| Наполнитель/армирование | - Стекло минеральное, 20% наполнитель по весу
|
| Характеристики | - Огнестойкий
- Хорошие электрические свойства
- Хорошая плавность
- Хорошая жесткость
- Хорошая прочность
- Без галогенов
- Высокая термостойкость
- Низкий уровень дыма
|
| Используется | - Электрическое/электронное применение
|
| Внешний вид | |
| Формы | |
| Метод обработки | |
| Код маркировки деталей (ISO 11469) | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Плотность | 1.90 | g/cm³ | ISO 1183 |
| Формовочная усадка | | | |
| -- | 0.50 | % | ISO 2577 |
| -- 1 | 0.0 | % | DIN 53464 |
| Поглощение воды (Saturation, 23°C) | < 0.30 | % | ISO 62 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Модуль растяжения (Compression Molded) | 13000 | MPa | ISO 527-2 |
| Tensile Stress (Yield, Compression Molded) | 31.0 | MPa | ISO 527-2 |
| Флекторный модуль (Compression Molded) | 10000 | MPa | ISO 178 |
| Флекторный стресс (Compression Molded) | 100 | MPa | ISO 178 |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Ударная прочность (Compression Molded) | 23 | kJ/m² | ISO 179 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | > 150 | °C | ISO 75-2/A |
| Температура непрерывного использования | 180 | °C | Internal Method |
| Температура перехода стекла | 185 | °C | DSC |
| CLTE-
Поток | 1.0E-5 | cm/cm/°C | ISO 11359-2 |
| Электрический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельное сопротивление поверхности | 1.0E+13 | ohms | IEC 60093 |
| Сопротивление громкости | 1.0E+16 | ohms·cm | IEC 60093 |
| Электрическая прочность | 40 | kV/mm | IEC 60243-1 |
| Коэффициент рассеивания | 0.010 | | IEC 60250 |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Воспламеняемость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Огнестойкость (3.00 mm) | HB | | UL 94 |
| Индекс кислорода | 22 | % | ISO 4589-2 |
| Инъекция | Номинальное значение | Единица измерения | |
|---|
| Температура формы | 135 to 150 | °C | |
| Давление впрыска | 2.00 to 8.00 | MPa | |
| Примечание |
|---|
| 1 . | Post Molding Shrinkage |
| Тип материала |
Категория |
Производитель |
|
BMC T40(20) |
Polyester, TS |
Bulk Molding Compounds, Inc.
|
|
En Chuan 6021H |
Polyester, TS |
En Chuan Chemical Industries Co,. Ltd.
|
|
Generic Polyester, TS - Glass Fiber |
Polyester, TS |
Generic
|
|
BMC 620X |
Polyester, TS |
Bulk Molding Compounds, Inc.
|
|
Ad-Tech Polyester NO. 17 |
Polyester, TS |
Ad-Tech Plastic Systems Corp.
|
|
En Chuan 6120TA-ISO |
Polyester, TS |
En Chuan Chemical Industries Co,. Ltd.
|