Описание материалов:
Menzolit® BMC 1100 is a bulk moulding compound based on unsaturated polyester resin. The product is glass fibre reinforced and contains mineral fillers. In case of fire the product doesn't melt, neither does it form droplets nor is smoke generation excessive. The material is compression moulded in heated steel moulds. It is recommended to work with chrome plated tools. The product contains no halogens.
Menzolit® BMC 1100 is a special BMC for high strength application. The glass content is set to a level that provides sufficient mouldability with high strength and stiffness properties. The selection of the resin and glass fibres provide good properties at high mechanical loads even if they are cyclic or impact like. The fire retardancy level HB according to the UL 94 is achieved. Typical applications are functional components for the automotive industry and chemical engineering. The material is especially suited for highly loaded or fast moving components.
| Главная Информация | |
|---|
| Наполнитель/армирование | - Стекло \ минеральное, 26% наполнитель по весу
|
| Характеристики | - Огнестойкий
- Хорошая плавность
- Хорошая жесткость
- Хорошая прочность
- Без галогенов
- Высокая термостойкость
- Низкий уровень дыма
|
| Используется | - Автомобильные Приложения
- Инженерные приложения
|
| Внешний вид | |
| Формы | |
| Метод обработки | |
| Код маркировки деталей (ISO 11469) | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Плотность | 1.80 | g/cm³ | ISO 1183 |
| Формовочная усадка | | | |
| -- | 0.30 | % | ISO 2577 |
| -- 1 | 0.0 | % | DIN 53464 |
| Поглощение воды (Saturation, 23°C) | < 0.30 | % | ISO 62 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Модуль растяжения (Compression Molded) | 13000 | MPa | ISO 527-2 |
| Tensile Stress (Yield, Compression Molded) | 40.0 | MPa | ISO 527-2 |
| Флекторный модуль (Compression Molded) | 9000 | MPa | ISO 178 |
| Флекторный стресс (Compression Molded) | 130 | MPa | ISO 178 |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Ударная прочность (Compression Molded) | 35 | kJ/m² | ISO 179 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | > 150 | °C | ISO 75-2/A |
| Температура непрерывного использования | 170 | °C | Internal Method |
| Температура перехода стекла | 162 | °C | DSC |
| CLTE-
Поток | 1.0E-5 | cm/cm/°C | ISO 11359-2 |
| Электрический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельное сопротивление поверхности | 1.0E+12 | ohms | IEC 60093 |
| Сопротивление громкости | 1.0E+15 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Воспламеняемость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Огнестойкость (3.00 mm) | HB | | UL 94 |
| Температура зажигания провода свечения | 750 | °C | IEC 60695-2-13 |
| Индекс кислорода | 22 | % | ISO 4589-2 |
| Дополнительная информация | Номинальное значение | | Метод испытания |
|---|
| Glow Bar | Level BH 2 <= 95 | | IEC 60707-3 |
| Инъекция | Номинальное значение | Единица измерения | |
|---|
| Температура формы | 135 to 160 | °C | |
| Давление впрыска | 2.00 to 8.00 | MPa | |
| Примечание |
|---|
| 1 . | Post Molding Shrinkage |