Описание материалов:
Lustran ABS PG 298 resin is a plateable grade of ABS (acrylonitrile butadiene styrene) for use in automotive and general-purpose applications. This injection molding grade was designed specifically for improved thermocycle performance and outstanding plate adhesion. It provides a unique combination of flow and rigidity, with increased scratch resistance and increased resistance to deformation on plating racks. The resin is available in gray color only.
Lustran ABS PG 298 resin is used in the automotive industry for plated grilles, wheel covers, exterior mirror housings, and exterior trim. It is also used for decorative parts in the appliance and lawn and garden markets. As with any product, use of Lustran ABS PG 298 resin in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability.
| Главная Информация | |
|---|
| Характеристики | - Хорошая стабильность размеров
- Гальваническое покрытие
- Хорошая мобильность
- Хорошая адгезия
- Устойчивость к царапинам
- Средняя твердость
|
| Используется | - Применение в автомобильной области
- Автомобильные внешние части
|
| Рейтинг агентства | |
| Внешний вид | |
| Формы | |
| Метод обработки | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 1.06 | g/cm³ | ASTM D792 |
| Удельный объем | 0.940 | cm³/g | ASTM D792 |
| Массовый расход расплава (MFR) | | | ASTM D1238 |
| 220°C/10.0 kg | 19 | g/10 min | ASTM D1238 |
| 230°C/3.8 kg | 5.0 | g/10 min | ASTM D1238 |
| Формовочная усадка-
Поток | 0.40 - 0.60 | % | ASTM D955 |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость Роквелла (R-Scale) | 110 | | ASTM D785 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Модуль растяжения | | | ASTM D638 |
| -- 1 | 7580 | MPa | ASTM D638 |
| -- 2 | 2770 | MPa | ASTM D638 |
| Прочность на растяжение | | | |
| Yield | 40.0 | MPa | ASTM D638 |
| Yield | 43.0 | MPa | ISO 527-2 |
| Флекторный модуль | | | |
| -- 3 | 12500 | MPa | ASTM D790 |
| -- 4 | 2830 | MPa | ASTM D790 |
| -- | 2730 | MPa | ISO 178 |
| Flexural Strength | | | ASTM D790 |
| Yield 5 | 117 | MPa | ASTM D790 |
| Yield 6 | 78.6 | MPa | ASTM D790 |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Зубчатый изод Impact | | | |
| 23°C, 3.18 mm | 170 | J/m | ASTM D256 |
| -40°C 7 | 6.4 | kJ/m² | ISO 180/1A |
| 23°C 8 | 14 | kJ/m² | ISO 180/1A |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Температура отклонения при нагрузке | | | ASTM D648 |
| 0.45 MPa, unannealed, 3.18mm | 91.1 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 12.7mm, molded | 103 | °C | ASTM D648 |
| 0.45 MPa, annealed, 12.7mm | 100 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.18mm | 83.9 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 12.7mm, molded | 98.3 | °C | ASTM D648 |
| 1.8 MPa, annealed, 12.7mm | 97.2 | °C | ASTM D648 |
| Викат Температура размягчения | | | |
| -- | 110 | °C | ASTM D1525 9 |
| -- | 36.6 | °C | ISO 306/B50 |
| Воспламеняемость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Скорость горения 10(2.01 mm) | 48 | mm/min | SAE J1685 |
| Инъекция | Номинальное значение | Единица измерения | |
|---|
| Температура сушки | | | |
| A | 82.2 - 87.8 | °C | |
| B | 71.1 - 76.7 | °C | |
| Время сушки | | | |
| A | 2.0 | hr | |
| B | 4.0 | hr | |
| Рекомендуемая максимальная влажность | < 0.10 | % | |
| Рекомендуемый размер снимка | 50 - 75 | % | |
| Рекомендуемый Макс измельчения | 20 | % | |
| Задняя температура | 243 - 252 | °C | |
| Средняя температура | 249 - 257 | °C | |
| Передняя температура | 254 - 263 | °C | |
| Температура сопла | 254 - 263 | °C | |
| Температура обработки (расплава) | 260 - 277 | °C | |
| Температура формы | 48.9 - 60.0 | °C | |
| Давление впрыска | 68.9 - 110 | MPa | |
| Скорость впрыска | Slow | | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Тонаж зажима | 2.8 - 5.5 | kN/cm² | |
| Отношение винта L/D | 20.0:1.0 | | |
| Коэффициент сжатия винта | 2.5:1.0 | | |
| Инструкции по впрыску |
|---|
| Hold Pressure: 50 to 75% of Injection PressureScrew Speed: Moderate |
| Примечание |
|---|
| 1 . | Plated |
| 2 . | Unplated |
| 3 . | Plated |
| 4 . | Unplated |
| 5 . | Plated |
| 6 . | Unplated |
| 7 . | 4x10 mm bar |
| 8 . | 4x10 mm bar |
| 9 . | 标准 B (120°C/h), 压 力1 (10N) |
| 10 . | 2x100x355 mm |