- AGILITY™ 1001 Performance LDPE
AGILITY™ 1001 Performance LDPE
| Категория | LDPE, Low Density Polyethylene Resin |
| Производитель | The Dow Chemical Company |
| Торговая марка | AGILITY™ |
| Порт | Китай Шанхайский порт |
| Торговые условия | FOB, CFR, CIF |
| Платежное средство | L/C, T/T, Western Union |
L2BPzk_AGILITY-1001-Performance-LDPE.pdf  |
|
| Контактная информация |  Служба поддержки клиентов Вичат |
|
|
|
Описание материалов:
AGILITY™ 1001 Performance LDPE is a high pressure LDPE resin designed specifically to run at faster output rates on blown film lines in blends with LLDPE resins while maintaining bubble stability.
Main Characteristics:
Complies with:
Main Characteristics:
- Faster processing LDPE resin
- Designed for higher output rates in blends with LLDPE resins at 10-20% loading
- Optimized molecular structure gives improved optics in blends with LLDPE resins
Complies with:
- EU No 10/2011
- U.S.FDA 21 CFR 177.1520 (c) 2.2
- Canadian HPFB No Objection
| Главная Информация | |
|---|---|
| Рейтинг агентства |
|
| Формы |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Удельный вес | 0.920 | g/cm³ | ASTM D792 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 0.65 | g/10 min | ASTM D1238 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Толщина пленки протестирована | 25 | µm | |
| Энергия прокола пленки | 1.02 | J | |
| Сила прокола пленки | 31.1 | N | |
| Сопротивление проколу пленки | 4.96 | J/cm³ | Internal method |
| Прочность пленки | ASTM D882 | ||
| MD | 26.5 | J/cm³ | ASTM D882 |
| TD | 53.8 | J/cm³ | ASTM D882 |
| Сектантный модуль | ASTM D882 | ||
| 1% secant, MD | 236 | MPa | ASTM D882 |
| 2% secant, MD | 216 | MPa | ASTM D882 |
| 1% secant, TD | 297 | MPa | ASTM D882 |
| 2% secant, TD | 256 | MPa | ASTM D882 |
| Прочность на растяжение | ASTM D882 | ||
| MD : Yield | 27.6 | MPa | ASTM D882 |
| TD : Yield | 12.8 | MPa | ASTM D882 |
| MD : Fracture | 28.6 | MPa | ASTM D882 |
| TD : Fracture | 16.9 | MPa | ASTM D882 |
| Удлинение при растяжении | ASTM D882 | ||
| MD : Fracture | 120 | % | ASTM D882 |
| TD : Fracture | 440 | % | ASTM D882 |
| Ударное падение Dart | 70 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD | 270 | g | ASTM D1922 |
| TD | 95 | g | ASTM D1922 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Викат Температура размягчения | 94.0 | °C | ASTM D1525 |
| Температура плавления (DSC) | 109 | °C | Internal method |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Блеск (45°) | 54 | ASTM D2457 | |
| Haze | 9.0 | % | ASTM D1003 |
| Инструкции по экструзии |
|---|
| Fabrication Conditions For Blown Film: Screw Size: 3.5 in. Screw Type: DSB II Die Gap: 70 mil Melt Temperature: 398°F Output: 12 lb/hr/in. of die circumference Die Diameter: 8 in. Blow-Up Ratio: 2.5 to 1 Screw Speed: 56 rpm Frost Line Height: 37 in. |
| Тип материала | Категория | Производитель |
|---|---|---|
| TAISOX 6323F | LDPE | Formosa Plastics Corporation |
| DOW™ LDPE SC 7642 | LDPE | The Dow Chemical Company |
| OKITEN® 222 A | LDPE | DIOKI d.d. |
| Osterlene® LD-.25-918 | LDPE | Osterman & Company |
| Petrothene® NA957 | LDPE | LyondellBasell Industries |
| Petrothene® NA206000 (Injection Molding) | LDPE | LyondellBasell Industries |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved