DOW™ LDPE 310E
| Категория | LDPE, Low Density Polyethylene Resin |
| Производитель | The Dow Chemical Company |
| Торговая марка | DOW™ LDPE |
| Порт | Китай Шанхайский порт |
| Торговые условия | FOB, CFR, CIF |
| Платежное средство | L/C, T/T, Western Union |
mKVu9f_DOW-LDPE-310E.pdf  |
|
| Контактная информация |  Служба поддержки клиентов Вичат |
|
|
|
Описание материалов:
DOW LDPE 310E is a fractional melt index low density polyethylene resin. DOW LDPE 310E has been specially designed for superior processability on blown film lines leading to significant output improvements. The resin offers additionally excellent draw down. It can be used pure or in blends with LLDPE resins.
Applications:
Main Characteristics:
Complies with:
Slip Additive: 0 ppm
Antiblock Additive: 0 ppm
Applications:
- lamination film, shrink film, and stretch film
Main Characteristics:
- Excellent processability and draw down
- Good physical properties in blends with LLDPE
- Can be readily extruded using conventional blown film techniques at melt temperatures between 160 and 195°C
Complies with:
- U.S. FDA 21 CFR 177.1520 ( c )2.2
- EU, No 10/2011
- U.S. FDA-DMF
- Canadian HPFB No Objection
Slip Additive: 0 ppm
Antiblock Additive: 0 ppm
| Главная Информация | |
|---|---|
| Рейтинг агентства |
|
| Формы |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Удельный вес | 0.923 | g/cm³ | ASTM D792 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 0.75 | g/10 min | ASTM D1238 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Коэффициент трения | 0.50 - 0.70 | ASTM D1894 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Толщина пленки протестирована | 50 | µm | |
| Энергия прокола пленки (50 µm) | 1.80 | J | Internal method |
| Сила прокола пленки (50 µm) | 50.0 | N | Internal method |
| Сопротивление проколу пленки (50 µm) | 4.00 | J/cm³ | Internal method |
| Сектантный модуль | ASTM D882 | ||
| 2% secant, MD : 50 µm, blown film | 175 | MPa | ASTM D882 |
| 2% secant, TD : 50 µm, blown film | 185 | MPa | ASTM D882 |
| Прочность на растяжение | ASTM D882 | ||
| MD : Yield, 50 µm, blown film | 11.0 | MPa | ASTM D882 |
| TD : Yield, 50 µm, blown film | 11.0 | MPa | ASTM D882 |
| MD : Broken, 50 µm, blown film | 25.0 | MPa | ASTM D882 |
| TD : Broken, 50 µm, blown film | 23.0 | MPa | ASTM D882 |
| Удлинение при растяжении | ASTM D882 | ||
| MD : Broken, 50 µm, blown film | 390 | % | ASTM D882 |
| TD : Broken, 50 µm, blown film | 570 | % | ASTM D882 |
| Ударное падение Dart (50 µm, Blown Film) | 170 | g | ASTM D1709A |
| Elmendorf Tear Strength 1 | ASTM D1922 | ||
| MD : 50 µm, blown film | 350 | g | ASTM D1922 |
| TD : 50 µm, blown film | 260 | g | ASTM D1922 |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Блеск (45°, 50.0 µm, Blown Film) | 58 | ASTM D2457 | |
| Haze (50.0 µm, Blown Film) | 9.2 | % | ASTM D1003 |
| Экструзия | Номинальное значение | Единица измерения | |
|---|---|---|---|
| Температура расплава | 160 - 195 | °C |
| Инструкции по экструзии |
|---|
| 吹塑薄膜的制造条件： 螺杆类型：通用 输出：25 kg/h 模具直径：150 mm。 放大比：2.5 螺杆速度：77 rpm |
| Примечание | |
|---|---|
| 1 . | Method B |
| Тип материала | Категория | Производитель |
|---|---|---|
| Riblene® FL 39 F | LDPE | Versalis S.p.A. |
| SABIC® LDPE 2601X1 | LDPE | Saudi Basic Industries Corporation (SABIC) |
| MIRASON™ 403P | LDPE | Mitsui Chemicals, Inc. |
| ALCUDIA® LDPE 3235FG | LDPE | REPSOL |
| COSMOTHENE® L420 | LDPE | TPC, The Polyolefin Company (Singapore) Pte Ltd |
| MTEGRITY™ LDPE LD120AA | LDPE | M. Holland Company |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved