TOTAL Polyethylene Lotrène® Q2018 C
Описание материалов:
Lotrène ® Q2018 C is an ethylene-butene copolymer produced in a gas phase reactor. It is designed for delivering competitive performance in most cast film applications.
Lotrène ® Q2018 C can be processed at high output rates with moderate extrusion pressure, good bubble stability and gauge control on cast film machine designed for LLDPE.
Lotrène ® Q2018 C can advantageously be blended with LDPE or other PE resins used in blown film mono extrusion or coextrusion to improve film properties.
Lotrène ® Q2018 C is suited for many applications in the field of consumer, industrial, food or hygiene packaging as well as stretch film and non-packaging applications like agricultural films e.g. mulching films.
| Главная Информация | |
|---|
| Добавка | |
| Характеристики | - Бутене комномер
- Устойчивость к окислению
|
| Используется | - Упаковка
- Пленка
- Промышленное применение
- Сельскохозяйственное применение
- Пищевая упаковка
|
| Метод обработки | - Экструзионная пленка
- Выдувная пленка
- Коэкструзионное формование
- Литая пленка
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 0.918 | g/cm³ | ASTM D792 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Толщина пленки протестирована | 20 | µm | |
| Модуль растяжения | | | ISO 178 |
| 1% secant, MD
: 20 µm, cast film | 165 | MPa | ISO 178 |
| 1% secant, TD
: 20 µm, cast film | 170 | MPa | ISO 178 |
| Tensile Stress | | | ISO 527-3 |
| MD
: Yield, 20 µm, cast film | 9.70 | MPa | ISO 527-3 |
| TD
: Yield, 20 µm, cast film | 9.60 | MPa | ISO 527-3 |
| MD
: Fracture, 20 µm, cast film | 37.0 | MPa | ISO 527-3 |
| TD
: Fracture, 20 µm, cast film | 23.0 | MPa | ISO 527-3 |
| Удлинение при растяжении | | | ISO 527-3 |
| MD
: Fracture, 20 µm, cast film | 330 | % | ISO 527-3 |
| TD
: Fracture, 20 µm, cast film | 670 | % | ISO 527-3 |
| Ударное падение Dart 1(20 µm, Cast Film) | 35 | g | ISO 7765-1 |
| Elmendorf Tear Strength | | | ISO 6383-2 |
| MD
: 20.0 µm | 12.0 | kN/m | ISO 6383-2 |
| TD
: 20.0 µm | 193.0 | kN/m | ISO 6383-2 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Викат Температура размягчения 2 | 100 | °C | ASTM D1525 |
| Температура плавления | 121 | °C | Internal method |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Блеск (45°, 20.0 µm, Cast Film) | 92 | | ASTM D2457 |
| Haze (20.0 µm, Cast Film) | 1.8 | % | ISO 14782 |
| Экструзия | Номинальное значение | Единица измерения | |
|---|
| Температура расплава | 180 - 250 | °C | |
| Инструкции по экструзии |
|---|
| Line speed: > 400 m/minDie gap: > 0.8 mmFilm properties are measured on cast line with following parameters: 30 mm screw diameter, L/D = 30:1, die length = 600 mm, die gap = 0.8 mm, line speed = 50 m/min, temperature setting = 180-230°C. Melt temperature = 250 °C and Chill roll temperature = 25 °C |