ELITE™ NG 5400B
| Категория | EPE, Enhanced Polyethylene Resin |
| Производитель | The Dow Chemical Company |
| Торговая марка | ELITE™ |
| Порт | Китай Шанхайский порт |
| Торговые условия | FOB, CFR, CIF |
| Платежное средство | L/C, T/T, Western Union |
HvvAlE_ELITE-NG-5400B.pdf  |
|
| Контактная информация |  Служба поддержки клиентов Вичат |
|
|
|
Описание материалов:
ELITE™ NG 5400B is a Linear Low Density Polyethylene, 1-Octene copolymer, produced with the SOLUTION™ technology. This resin presents excellent tensile, tear and puncture resistance even at low temperatures with great gloss and clarity. It has a low seal initiation temperature with high seal performance.
Main Characteristics:
Main Characteristics:
- Film for packaging for frozen food
- Excellent mechanical properties even at low temperatures
- Low seal initiation temperature and high seal properties
- Excellent optics
- Suitable for food contact: Report # 690/05 issued by INAL according to MERCOSUR.
- Consult the regulation to obtain complete details
| Главная Информация | |
|---|---|
| Формы |
|
| Метод обработки |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Удельный вес | 0.916 | g/cm³ | ASTM D792 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Толщина пленки протестирована | 38 | µm | |
| Сопротивление проколу пленки (38 µm) | 10.0 | J/cm³ | Internal method |
| Сектантный модуль | ASTM D882 | ||
| 2% secant, MD : 38 µm | 134 | MPa | ASTM D882 |
| 2% secant, TD : 38 µm | 143 | MPa | ASTM D882 |
| Прочность на растяжение | ASTM D882 | ||
| MD : Yield, 38 µm | 10.0 | MPa | ASTM D882 |
| TD : Yield, 38 µm | 10.0 | MPa | ASTM D882 |
| MD : Fracture, 38 µm | 40.0 | MPa | ASTM D882 |
| TD : Fracture, 38 µm | 36.0 | MPa | ASTM D882 |
| Удлинение при растяжении | ASTM D882 | ||
| MD : Fracture, 38 µm | 750 | % | ASTM D882 |
| TD : Fracture, 38 µm | 930 | % | ASTM D882 |
| Ударное падение Dart (38 µm) | 1400 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 38 µm | 700 | g | ASTM D1922 |
| TD : 38 µm | 910 | g | ASTM D1922 |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Блеск (45°, 37.5 µm) | 64 | ASTM D2457 | |
| Haze (37.5 µm) | 9.0 | % | ASTM D1003 |
| Экструзия | Номинальное значение | Единица измерения | |
|---|---|---|---|
| Температура расплава | 232 | °C |
| Инструкции по экструзии |
|---|
| 吹塑薄膜的加工条件： 螺杆直径：63.5 mm（2.5 英寸）；24.5 L/D 模具间隙：1.8 mm（70 密尔） 熔体温度： 232°C (450°F) 输出：52 kg/h（113 磅/小时） 模具直径：152 mm（6 英寸） 放大比：2.5:1 螺杆速度：83 rpm 冷冻线高度：635 mm（25 英寸） |
| Тип материала | Категория | Производитель |
|---|---|---|
| ELITE™ AT 6202 | EPE | The Dow Chemical Company |
| ELITE™ 5960G1 | EPE | The Dow Chemical Company |
| ELITE™ 5230GC | EPE | The Dow Chemical Company |
| ELITE™ AT 6111 | EPE | The Dow Chemical Company |
| ELITE™ NG 5401B | EPE | The Dow Chemical Company |
| ELITE™ 5110G | EPE | The Dow Chemical Company |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved