MXSTEN® CV77518
| Категория | Plastic, Ethylene-based Plastomer , Plastomer |
| Производитель | Westlake Chemical Corporation |
| Торговая марка | MXSTEN® |
| Порт | Китай Шанхайский порт |
| Торговые условия | FOB, CFR, CIF |
| Платежное средство | L/C, T/T, Western Union |
HkSmSw_MXSTEN-CV77518.pdf  |
|
| Контактная информация |  Служба поддержки клиентов Вичат |
|
|
|
Описание материалов:
CV77518 resin is a polyethylene plastomer designed for blown and cast film extrusion that contains no slip and no antiblock additives. Films produced with this resin exhibit a very low seal initiation temperature with a broad hot tack window. Other features of this resin include higher stiffness, high melting point, and ease of processing for narrow die gaps.
Application/Uses:
Blown film
Cast film
Packaging
Application/Uses:
Blown film
Cast film
Packaging
| Главная Информация | |
|---|---|
| Характеристики |
|
| Используется |
|
| Рейтинг агентства |
|
| Формы |
|
| Метод обработки |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Плотность | 0.910 | g/cm³ | ASTM D4883 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Толщина пленки протестирована | 25 | µm | |
| Сектантный модуль 1 | ASTM D882 | ||
| 1% secant, MD : 25 µm, blown film | 152 | MPa | ASTM D882 |
| 1% secant, TD : 25 µm, blown film | 172 | MPa | ASTM D882 |
| Прочность на растяжение 2 | ASTM D882 | ||
| MD : Broken, 25 µm, blown film | 35.0 | MPa | ASTM D882 |
| TD : Broken, 25 µm, blown film | 40.0 | MPa | ASTM D882 |
| Удлинение при растяжении 3 | ASTM D882 | ||
| MD : Broken, 25 µm, blown film | 700 | % | ASTM D882 |
| TD : Broken, 25 µm, blown film | 1200 | % | ASTM D882 |
| Ударное падение Dart 4(25 µm, Blown Film) | 400 | g | ASTM D1709A |
| Elmendorf Tear Strength 5 | ASTM D1922 | ||
| MD : 25 µm, blown film | 300 | g | ASTM D1922 |
| TD : 25 µm, blown film | 550 | g | ASTM D1922 |
| Температура инициализации уплотнения 6(25 µm, Blown Film) | 88.0 | °C | Internal method |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Блеск (45°, 25.4 µm, Blown Film) | 55 | ASTM D2457 | |
| Haze (25.4 µm, Blown Film) | 13 | % | ASTM D1003 |
| Дополнительная информация |
|---|
| Extrusion conditions used to produce 1 mil (0.025 mm) film include a 6" die, 2.5" 24:1 L:D barrier screw, 2.4:1 BUR, 100-mil die gap, 15" frostline height, 400° F melt temperature, and 7.5 lb/hr/inch die output. Density results are on Base Resin. |
| Примечание | |
|---|---|
| 1 . | Test run at 23°C (73°F) and 50% relative humidity |
| 2 . | Test run at 23°C (73°F) and 50% relative humidity |
| 3 . | Test run at 23°C (73°F) and 50% relative humidity |
| 4 . | Test run at 23°C (73°F) and 50% relative humidity |
| 5 . | Test run at 23°C (73°F) and 50% relative humidity |
| 6 . | Seal initiation temperature is the temperature at which 200 g/inch seal strength is achieved. |
| Тип материала | Категория | Производитель |
|---|---|---|
| MXSTEN® CV77526 | Plastomer | Westlake Chemical Corporation |
| Exact™ 3132 | Plastomer | ExxonMobil Chemical |
| Exact™ 4053 Cast | Plastomer | ExxonMobil Chemical |
| ICORENE® 2910 | Plastomer | ICO Polymers EMEA, A Division of A. Schulman |
| Queo™ 0219 | Plastomer | Borealis AG |
| Queo™ 0230 | Plastomer | Borealis AG |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved