Описание материалов:
Diofan® B 204 is a PVDC latex with outstanding impermeability to gases and moisture. It is particularly recommended for coatings on plastic films.
| Главная Информация | |
|---|
| Используется | |
| Рейтинг агентства | - EC 1907/2006 (REACH)
- Управление по санитарному надзору за качеством пищевых продуктов и медикаментов 21 CFR 175,320
- Управление по санитарному надзору за качеством пищевых продуктов и медикаментов 21 CFR 177,1630
- Европа без 10/2011
|
| Внешний вид | |
| Формы | |
| Физический | Номинальное значение | Единица измерения | |
|---|
| PH | 1.5 | | |
| Поверхностное натяжение-
Тренд вспенивания | 45 | mN/m | |
| Формирование пленки-
Температура формовки пленки | 14 | °C | |
| Содержание твердых веществ | 51 | % | |
| Плотность | | | |
| Dispersion (wet) | 1.270 | g/cm³ | |
| Coating (dry) | 1.650 | g/cm³ | |
| Тип эмульсии | anion | | |
| Вязкость-
Динамический
(20 °C) | 17 | mPa·s | |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Скорость передачи кислорода-
85% RH 1 | 11 | cm³/m²/bar/24 hr | ASTM D3985 |
| Порог теплового уплотнения-
0,4 Н/см 2 | 124 | °C | |
| Максимальное сопротивление теплового уплотнения-
20 psi - 1s - 1 с подогревом 3 | 1.0 | N/cm | |
| Дополнительная информация | Номинальное значение | Единица измерения | |
|---|
| Срок годности (23 °C) | 12 | month | |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Коэффициент трения 4(vs. Itself - Dynamic) | 0.35 | | ASTM D1894 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Скорость передачи водяного пара 5(38°C, 90% RH, 1.0 µm) | 11 | g/m²/24 hr | ASTM F1249 |
| Дополнительная информация | Номинальное значение | Единица измерения | |
|---|
| DELIVERY AND STORAGE
Diofan® B 204 is delivered in bulk or in Intermediate Bulk Containers (IBC). Bulk supplied latex should be stored in reservoirs made of suitable stainless steel, HDPE, rigid PVC or glass fiber-reinforced polyester.
Contact of anionic Diofan® dispersion with metals like iron, zinc, aluminum and copper as well as alloys such as brass and bronze must be avoided.
Keep the vessels tightly closed to prevent drying through evaporation. Store the product ideally between 5°C and 25°C (41 °F and 77°F) to avoid degradation.
PROCESSING - DRYING
Diofan® B 204 can be processed with different coating techniques, including reverse gravure roll and air knife coating systems.
When coated on plastic films, Diofan® B 204 should be formulated with wax and silica in order to improve the blocking and slip properties of the finished coating.
Diofan® coatings requires adequate drying conditions, since in general higher temperatures will contribute to better barrier properties.
FOOD AND DRUG LEGISLATIONS
Some agency ratings are listed on page 1. Necessary certification will be provided upon request.
ISO CERTIFICATION
The implemented management system for the production, internal transfer and delivery, design and development of Diofan® vinylidene chloride copolymers (PVDC) produced in Tavaux has been assessed and found to meet the requirements of ISO 9001: 2008, ISO 14001: 2004 and OHSAS 18001: 2007. |
| Примечание |
|---|
| 1 . | BOPP coating; Weight of paint: 2.7g/m; Additive package: 20 g/kg wax 3 g/kg silicon |
| 2 . | Heat sealing condition: 20psi-1s-1 heating clamp |
| 3 . | Heat sealing condition: 20psi-1s-1 heating clamp |
| 4 . | BOPP coating; Weight of paint: 2.7g/m; Additive package: 20 g/kg wax 3 g/kg silicon |
| 5 . | Coating on PET film. Diofan® coating weight dry: 2.5 g/m²; used additive package: 5 g/kg wax + 5 g/kg silica |