Braskem PE TN7006
| Категория | LDPE, Low Density Polyethylene |
| Производитель | Braskem |
| Торговая марка | Braskem PE |
| Порт | Китай Шанхайский порт |
| Торговые условия | FOB, CFR, CIF |
| Платежное средство | L/C, T/T, Western Union |
GhaHeH_Braskem-PE-TN7006.pdf  |
|
| Контактная информация |  Служба поддержки клиентов Вичат |
|
|
|
Описание материалов:
TN7006 is a low-density polyethylene (LDPE) specially developed for coextruded films and lamination. The resin presents a great combination among mechanical, optical and stiffness properties. Besides TN7006 has low gels content which ensure a production of excellent appearance films. This product is identified as PE 114 according to ASTM D-4976-04a standard specification.
Additives:
No additives
Application:
High clarity films for coextruded food packaging, such as: cheese, meat, sausages, sliced ham, etc. Cast films for table cloth, curtains and laminated tissues. Flexible bottles for solids, liquids or pasties products for hygiene and cleanness.
Additives:
No additives
Application:
High clarity films for coextruded food packaging, such as: cheese, meat, sausages, sliced ham, etc. Cast films for table cloth, curtains and laminated tissues. Flexible bottles for solids, liquids or pasties products for hygiene and cleanness.
| Главная Информация | |
|---|---|
| Характеристики |
|
| Используется |
|
| Рейтинг агентства |
|
| Метод обработки |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Удельный вес | 0.924 | g/cm³ | ASTM D792 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 0.60 | g/10 min | ASTM D1238 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Толщина пленки протестирована | 50 | µm | |
| Сектантный модуль | ASTM D882 | ||
| 2% Secant, MD : 50 µm, Blown Film | 140 | MPa | |
| 2% Secant, TD : 50 µm, Blown Film | 170 | MPa | |
| Прочность на растяжение | ASTM D882 | ||
| MD : Break, 50 µm, Blown Film | 25.0 | MPa | |
| TD : Break, 50 µm, Blown Film | 20.0 | MPa | |
| Удлинение при растяжении | ASTM D882 | ||
| MD : Break, 50 µm, Blown Film | 350 | % | |
| TD : Break, 50 µm, Blown Film | 700 | % | |
| Ударное падение Dart (50 µm, Blown Film) | 170 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 50 µm, Blown Film | 310 | g | |
| TD : 50 µm, Blown Film | 250 | g |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Блеск | ASTM D2457 | ||
| 45°, 50.0 µm, Blown Film | 60 | ||
| 60°, 50.0 µm, Blown Film | 86 | ||
| Haze (50.0 µm, Blown Film) | 8.5 | % | ASTM D1003 |
| Дополнительная информация | Номинальное значение | Единица измерения | |
|---|---|---|---|
| Температура выдувного формования 1 | |||
| Mass Temperature | 180 to 185 | °C | |
| Temperature Profile | 150 to 185 | °C |
| Примечание | |
|---|---|
| 1 . | 1.0mm Die Gap, 2.0 to 3.0:1 Blow Up Ratio |
| Тип материала | Категория | Производитель |
|---|---|---|
| Sasol Polymers PE LT033 (Film Extrusion) | LDPE | Sasol Polymers |
| Braskem PE STS7006 | LDPE | Braskem America Inc. |
| AT 280 | LDPE | Celanese EVA Performance Polymers |
| DINALEN® 50 | LDPE | DIOKI d.d. |
| Kemcor LD 6215 | LDPE | Qenos Pty Ltd |
| MARPOL® LDM 740 | LDPE | Marco Polo International, Inc. |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved