Amodel® A-6135 HN

Категория PPA, Polyphthalamide
Производитель Solvay Specialty Polymers
Торговая марка Amodel®
Порт Китай Шанхайский порт
Торговые условия FOB, CFR, CIF
Платежное средство L/C, T/T, Western Union
PDF GfcVdb_Amodel-A-6135-HN.pdf
Контактная информация
EMAIL US sales@su-jiao.com

Служба поддержки клиентов Вичат
Описание материалов:
Amodel® A-6135 HN polyphthalamide (PPA) is a 35% glass reinforced resin that is heat stabilized, lubricated and hot-water moldable. Key properties of the resin are high heat resistance, high strength and stiffness over a broad temperature range. It also exhibits low moisture absorption, excellent chemical resistance and excellent electrical properties.

Amodel® A-6135 HN resin is ideal for automotive electrical and electronic applications, including connectors, sockets, switches and sensors. It is also a good choice for under-hood enclosures that protect critical control systems such as anti-lock brakes, traction control, steering, electronic engine control, transmission and chassis control units.

  • Black: A-6135 HN BK 324
  • Natural A-6135 HS NT
Главная Информация
Наполнитель/армирование
  • Армированный стекловолокном материал, 35% наполнитель по весу
Добавка
  • Стабилизатор тепла
Характеристики
  • Низкая гигроскопичность
  • Жесткий, высокий
  • Жесткий, хороший
  • Высокая прочность
  • Хорошее сопротивление ползучести
  • Хорошая мобильность
  • Хорошая химическая стойкость
  • Теплостойкость, высокая
  • Формируемость горячей воды
  • Термическая стабильность
Используется
  • Оборудование для газонов и сада
  • Электрическое/электронное применение
  • Электрический корпус
  • Электропитание/другие инструменты
  • Детали клапана/клапана
  • Промышленные компоненты
  • Промышленное применение
  • Машина/механические детали
  • Замена металла
  • Соединитель
  • Детали под крышкой двигателя автомобиля
  • Автомобильная электроника
  • Применение в автомобильной области
  • Универсальный
  • Чехол
Соответствие RoHS
  • Свяжитесь с производителем
Внешний вид
  • Черный
Формы
  • Частицы
Метод обработки
  • Температура воды литье под давлением
Многоточечные данные
  • Изоляционный стресс против деформации (ISO 11403-1)
ФизическийСухойСостояниеЕдиница измеренияМетод испытания
Плотность 1.45--g/cm³ISO 1183/A
Формовочная усадка
     Flow 0.60--%ASTM D955
     Transverse flow 0.90--%ASTM D955
     Vertical flow direction 1.0--%ISO 294-4
     Flow direction 0.50--%ISO 294-4
Поглощение воды
     24 hr 0.30--%ASTM D570
     23°C, 24 hr 0.29--%ISO 62
ТвердостьСухойСостояниеЕдиница измеренияМетод испытания
Твердость Роквелла (R-Scale)125--ASTM D785
МеханическиеСухойСостояниеЕдиница измеренияМетод испытания
Модуль растяжения
     -- 1380012200MPaASTM D638
     23°C 11500--MPaISO 527-2
     100°C 7310--MPaISO 527-2
     150°C 6270--MPaISO 527-2
     175°C 5310--MPaISO 527-2
Tensile Stress
     Fracture, 23°C 211--MPaISO 527-2
     Fracture, 100°C 121--MPaISO 527-2
     Fracture, 150°C 92.4--MPaISO 527-2
     Fracture, 175°C 82.0--MPaISO 527-2
     -- 203176MPaASTM D638
Удлинение при растяжении
     Fracture 1.92.1%ASTM D638
     Fracture, 23°C 2.0--%ISO 527-2
     Fracture, 100°C 4.3--%ISO 527-2
     Fracture, 150°C 4.9--%ISO 527-2
     Fracture, 175°C 4.7--%ISO 527-2
Флекторный модуль
     -- 1140011000MPaASTM D790
     23°C 11400--MPaISO 178
     100°C 6600--MPaISO 178
     150°C 4900--MPaISO 178
     175°C 4600--MPaISO 178
Flexural Strength
     -- 310249MPaASTM D790
     3.5% strain, 23°C 300--MPaISO 178
     3.5% strain, 100°C 170--MPaISO 178
     3.5% strain, 150°C 123--MPaISO 178
     3.5% strain, 175°C 112--MPaISO 178
Прочность на сжатие 148--MPaASTM D695
Прочность сдвига 87.673.8MPaASTM D732
Poisson's Ratio 0.39--ASTM E132
ВоздействиеСухойСостояниеЕдиница измеренияМетод испытания
Ударная прочность (23°C)9.2--kJ/m²ISO 179/1eA
Charpy Unnotched Impact Strength (23°C)60--kJ/m²ISO 179/1eU
Зубчатый изод Impact
     -- 8569J/mASTM D256
     23°C 9.1--kJ/m²ISO 180
Незубчатый изод Impact
     -- 800--J/mASTM D256
     23°C 62--kJ/m²ISO 180
ТепловойСухойСостояниеЕдиница измеренияМетод испытания
Heat Deflection Temperature
     0.45 MPa, not annealed 303--°CISO 75-2/B
     1.8 MPa, not annealed 288--°CISO 75-2/A
     1.8 MPa, annealed, 3.20mm 291--°CASTM D648
Температура плавления 310--°CASTM D570, ISO 11357-3
Линейный коэффициент теплового расширения ASTM E831
     Flow : 0 to 100°C 2.2E-5--cm/cm/°CASTM E831
     Flow : 100 to 200°C 1.6E-5--cm/cm/°CASTM E831
     Lateral : 0 to 100°C 6.1E-5--cm/cm/°CASTM E831
     Lateral : 100 to 200°C 1.0E-4--cm/cm/°CASTM E831
ИнъекцияСухойЕдиница измерения
Температура сушки 120°C
Время сушки 4.0hr
Рекомендуемая максимальная влажность 0.045%
Задняя температура 316 - 321°C
Передняя температура 327 - 332°C
Температура обработки (расплава) 321 - 335°C
Температура формы 65.6 - 93.3°C
Инструкции по впрыску
Injection Rate: 3 to 6 in/secHolding Pressure: 50% of injection pressureStorage: Amodel® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Amodel® resins be dried prior to molding following the recommendations found in this datasheet and/or in the Amodel® processing guide.
Тип материала Категория Производитель
SEPAZ™ 100L PPA Mando Advanced Materials Co., Ltd.
Tecomid® HT NT40 GR60 NL HS PPA Eurotec Engineering Plastics
HiFill® PPA GF35 IM AHWR PPA Techmer Engineered Solutions
RTP 4006 PPA RTP Company
LUVOCOM® 20-8333 PPA Lehmann & Voss & Co.
LNP™ THERMOCOMP™ UC008H compound PPA SABIC Innovative Plastics
Получите информацию об этом продукте следующим способом.
Телефон+086 13424755533
EMAIL US sales@su-jiao.com

Служба поддержки клиентов Вичат
Copyright © russianpolymer.com All Rights Reserved
Получите информацию об этом продукте следующим способом.
+08613424755533
sales@su-jiao.com

Служба поддержки клиентов Вичат
Свяжитесь с нами