Menzolit® AdvancedSMC 0400
Описание материалов:
Menzolit® AdvancedSMC 0400 is a special low profile SMC for applications within the automotive industry. It satisfies the surface quality needed for automotive body panels. It complies with all automotive regulations, C-Emissions are minimized. To achieve the highest surface quality, we recommend that tool surfaces are mirror polished. The temperature resistance of AdvancedSMC allows online painting at standard bake temperatures. The product shows very good adhesion to paint or In Mould Coating (IMC). Because of its zero shrink properties, warpage is eliminated and parts reproducing the dimensions of the cold mould can be produced. Figures given apply to a quasi isotropic 6-layer [0/90/45/-45/90/0] design, different layer designs are possible, please contact our R&D departement. Please check storage conditions printed on packaging label.
| Главная Информация | |
|---|
| Наполнитель/армирование | - Минеральный наполнитель
- Армированный материал из углеродного волокна
|
| Характеристики | - Хорошая стабильность размеров
- Низкий уровень защиты
- Низкий дым
- Распылитель
- Хорошая адгезия
- Низкое сжатие
- Без галогенов
- Отличный внешний вид
|
| Используется | - Применение в автомобильной области
|
| Формы | |
| Код маркировки деталей (ISO 11469) | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Плотность | 1.67 | g/cm³ | ISO 1183 |
| Формовочная усадка (0°C) | -0.012 | % | ISO 294-4 |
| Поглощение воды (Saturation, 23°C) | 1.0 | % | ISO 62 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Модуль растяжения | | | ISO 527-2 |
| 0°C, compression molding | 32000 | MPa | ISO 527-2 |
| 90°C, compression molding | 32000 | MPa | ISO 527-2 |
| Tensile Stress | | | ISO 527-2 |
| Yield, 0°C, compression molding | 200 | MPa | ISO 527-2 |
| Yield, 90°C, compression molding | 200 | MPa | ISO 527-2 |
| Растяжимое напряжение | | | ISO 527-2 |
| Fracture, 0°C, compression molding | 1.4 | % | ISO 527-2 |
| Fracture, 90°C, compression molding | 2.0 | % | ISO 527-2 |
| Флекторный модуль | | | ISO 178 |
| 0°C, compression molding | 40000 | MPa | ISO 178 |
| 90°C, compression molding | 20000 | MPa | ISO 178 |
| Флекторный стресс | | | ISO 178 |
| 0°C, compression molding | 400 | MPa | ISO 178 |
| 90°C, compression molding | 400 | MPa | ISO 178 |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Ударная прочность | | | ISO 179 |
| 0°C, compression molding | 70 | kJ/m² | ISO 179 |
| 90°C, compression molding | 70 | kJ/m² | ISO 179 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Температура перехода стекла | 185 | °C | DSC |
| CLTE-
Поток | | | ISO 11359-2 |
| 0°C | 1.7E-6 | cm/cm/°C | ISO 11359-2 |
| 90°C | 1.7E-6 | cm/cm/°C | ISO 11359-2 |
| Воспламеняемость | Номинальное значение | | Метод испытания |
|---|
| Огнестойкость (2.00 mm) | HB | | UL 94 |
| Дополнительная информация |
|---|
| Post Moulding Shrinkage, DIN 53464: 0%Heat Distortion Temperature, EN ISO 75-2: >200°CContinuous Service Temperature, Menzolit Method: 180°CFiber Content UD, total, EN ISO 1172, 90°C: 38%Fiber Content UD, total, EN ISO 1172, 0°C: 54%Poison's Ratio, Menzolit Method, 0°C: 0.3Poison's Ratio, Menzolit Method, 90°C: 0.3Matrix Crazing Strain, Menzolit Method: 0.5%Compression Strength, EN ISO 14126, 0°C: 200 MPaThe value listed as Glass Transition Temp DSC, was tested in accordance with ISO 11357-2.The values listed as Flexural Strength and Lfexural Modulus, ISO 178, were tested in accordance with EN ISO 14125 |
| Инъекция | Номинальное значение | Единица измерения | |
|---|
| Температура формы | 155 - 160 | °C | |
| Давление впрыска | 10.0 - 16.0 | MPa | |