VESTAMID® NRG 2901 black
| Категория | PA12, Polyamide 12 , Nylon 12 |
| Производитель | Evonik Industries AG |
| Торговая марка | VESTAMID® NRG |
| Порт | Китай Шанхайский порт |
| Торговые условия | FOB, CFR, CIF |
| Платежное средство | L/C, T/T, Western Union |
G6F7TD_VESTAMID-NRG-2901-black.pdf  |
|
| Контактная информация |  Служба поддержки клиентов Вичат |
|
|
|
Описание материалов:
For gas pipe fittings
VESTAMID® NRG 2901 is a high molecular, heat stabilized compound with exceptional mold release properties. Additionally, VESTAMID®NRG 2901 is nucleated to reduce the cycle time and shrinkage of molded parts.
Generally mechanical properties of compounds based on PA 12 vary little with changing humidity due to their low-moisture absorption.
Parts made of this semi-crystalline material are characterized by exceptional impact strength, high abrasion resistance, low friction and good chemical resistance.
We recommend a processing temperature between 230°C (446°F) and 260°C (500°F) - in some cases up to 280°C (536°F) - during the injection molding process.The mold temperature should be within a range of 60°C (140°F) to 100°C (212°F).
Drying at 80°C (176°F) for 2 hours to 4 hours before processing is recommended.
Polyamide 12 is a high performance thermoplastic polymer with increased performance characteristics that translates into safe operations over the life of the installed pipeline.
It has a considerable record of safe and proven experience in many demanding applications, including fuel lines in passenger cars, air brake tubing in trucks and off-shore applications.
VESTAMID® NRG 2901 is a high molecular, heat stabilized compound with exceptional mold release properties. Additionally, VESTAMID®NRG 2901 is nucleated to reduce the cycle time and shrinkage of molded parts.
Generally mechanical properties of compounds based on PA 12 vary little with changing humidity due to their low-moisture absorption.
Parts made of this semi-crystalline material are characterized by exceptional impact strength, high abrasion resistance, low friction and good chemical resistance.
We recommend a processing temperature between 230°C (446°F) and 260°C (500°F) - in some cases up to 280°C (536°F) - during the injection molding process.The mold temperature should be within a range of 60°C (140°F) to 100°C (212°F).
Drying at 80°C (176°F) for 2 hours to 4 hours before processing is recommended.
Polyamide 12 is a high performance thermoplastic polymer with increased performance characteristics that translates into safe operations over the life of the installed pipeline.
It has a considerable record of safe and proven experience in many demanding applications, including fuel lines in passenger cars, air brake tubing in trucks and off-shore applications.
| Главная Информация | |
|---|---|
| Добавка |
|
| Характеристики |
|
| Внешний вид |
|
| Метод обработки |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Плотность (23°C) | 1.01 | g/cm³ | ISO 1183 |
| Формовочная усадка | ISO 294-4 | ||
| Across Flow : 80°C, 2.00 mm | 1.2 | % | |
| Flow : 80°C, 2.00 mm | 0.67 | % |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Модуль растяжения | 1500 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 45.0 | MPa | ISO 527-2 |
| Растяжимое напряжение | ISO 527-2 | ||
| Yield | 5.0 | % | |
| Break | > 50 | % |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Ударная прочность | ISO 179/1eA | ||
| -30°C, Complete Break | 7.0 | kJ/m² | |
| 23°C, Complete Break | 7.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 140 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 50.0 | °C | ISO 75-2/A |
| Викат Температура размягчения | |||
| -- | 175 | °C | ISO 306/A |
| -- | 150 | °C | ISO 306/B |
| Инъекция | Номинальное значение | Единица измерения | |
|---|---|---|---|
| Температура сушки | 80.0 | °C | |
| Время сушки | 2.0 to 4.0 | hr | |
| Температура обработки (расплава) | 230 to 280 | °C | |
| Температура формы | 60.0 to 100 | °C |
| Тип материала | Категория | Производитель |
|---|---|---|
| Rilsamid® AESNO TL | Nylon 12 | Arkema |
| Grilamid® XE 4158 nat | Nylon 12 | EMS-GRIVORY |
| Latamid 12 G/50 | Nylon 12 | LATI S.p.A. |
| VESTAMID® Care ML24 | Nylon 12 | Evonik Industries AG |
| Titalon® 3315TF | Nylon 12 | Titan Plastics Compounds Co., Ltd. |
| Generic Nylon 12 | Nylon 12 | Generic |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved