Описание материалов:
Vydyne 20NSP BLK is a general-purpose, highly nucleated, lubricated PA66 resin. Available in black, it is designed to crystallize rapidly in order to reduce cycle times and increase productivity through faster part set-up. The higher crystalline structure will increase tensile modulus and strength, reduce elongation and may slightly lower mold shrinkage when compared to standard general-purpose non nucleated PA66. The rapid crystallization of Vydyne 20NSP BLK resin may allow part ejection at a higher temperature compared to general-purpose PA66. Critical factors unique to each application such as mold design, part design, tolerances and other factors will dictate ultimate cycle time benefits. It is recommended to check critical part dimensions against specifications before adopting shorter molding cycles. Vydyne 20NSP BLK resin has an external lubricant for improved machine feed and an internal lubricant for improved mold release.
Typical Applications/End Uses:
End uses for Vydyne 20NSP BLK include terminal blocks, bearings, control cams, electrical connectors, housings, cable ties, fasteners, switch components and industrial parts that require chemical resistance, stiffness, wear resistance and rigidity.
| Главная Информация | |
|---|
| Добавка | |
| Характеристики | - Цикл быстрого формования
- Общее назначение
- Хороший выпуск пресс-формы
- Хорошая жесткость
- Высокая жесткость
- Смазка
- Ядро
|
| Используется | - Подшипники
- Камеры
- Разъемы
- Крепежные детали
- Общее назначение
- Корпуса
- Промышленное применение
|
| Рейтинг агентства | - Астм д 4066 PA0131
- Астм д 6779 PA0131
- FED L-P-410A
|
| Соответствие RoHS | |
| Номер файла UL | |
| Внешний вид | |
| Формы | |
| Метод обработки | |
| Физический | Сухой | Состояние | Единица измерения | Метод испытания |
|---|
| Плотность | 1.14 | -- | g/cm³ | ISO 1183 |
| Формовочная усадка | | | | ISO 294-4 |
| Across Flow
: 23°C, 2.00 mm | 1.6 | -- | % | |
| Flow
: 23°C, 2.00 mm | 1.4 | -- | % | |
| Поглощение воды | | | | ISO 62 |
| 23°C, 24 hr | 1.2 | -- | % | |
| Equilibrium, 23°C, 50% RH | 2.4 | -- | % | |
| Уличная пригодность | f2 | -- | | UL 746C |
| Механические | Сухой | Состояние | Единица измерения | Метод испытания |
|---|
| Модуль растяжения (23°C) | 3800 | 2500 | MPa | ISO 527-2 |
| Tensile Stress | | | | ISO 527-2 |
| Yield, 23°C | 95.0 | 60.0 | MPa | |
| Break, 23°C | 75.0 | 50.0 | MPa | |
| Растяжимое напряжение (Yield, 23°C) | 5.0 | 15 | % | ISO 527-2 |
| Номинальное растяжение при разрыве (23°C) | 13 | 20 | % | ISO 527-2 |
| Флекторный модуль (23°C) | 3200 | 1300 | MPa | ISO 178 |
| Flexural Strength (23°C) | 100 | 35.0 | MPa | ISO 178 |
| Poisson's Ratio | 0.40 | -- | | ISO 527-2 |
| Воздействие | Сухой | Состояние | Единица измерения | Метод испытания |
|---|
| Ударная прочность | | | | ISO 179/1eA |
| -30°C | 5.0 | 5.0 | kJ/m² | |
| 23°C | 6.0 | 15 | kJ/m² | |
| Charpy Unnotched Impact Strength | | | | ISO 179/1eU |
| -30°C | No Break | No Break | | |
| 23°C | No Break | No Break | | |
| Зубчатый изод ударная прочность | | | | ISO 180 |
| -30°C | 5.0 | 5.0 | kJ/m² | |
| 23°C | 6.0 | 15 | kJ/m² | |
| Тепловой | Сухой | Состояние | Единица измерения | Метод испытания |
|---|
| Heat Deflection Temperature | | | | |
| 0.45 MPa, Unannealed | 230 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 90.0 | -- | °C | ISO 75-2/A |
| Температура плавления | 260 | -- | °C | ISO 11357-3 |
| CLTE | | | | ISO 11359-2 |
| Flow
: 23 to 55°C, 2.00 mm | 1.0E-4 | -- | cm/cm/°C | |
| Transverse
: 23 to 55°C, 2.00 mm | 1.0E-4 | -- | cm/cm/°C | |
| RTI Elec | | | | UL 746 |
| 0.400 mm | 130 | -- | °C | |
| 0.710 mm | 130 | -- | °C | |
| 1.50 mm | 130 | -- | °C | |
| 3.00 mm | 130 | -- | °C | |
| RTI Imp | | | | UL 746 |
| 0.400 mm | 75.0 | -- | °C | |
| 0.710 mm | 75.0 | -- | °C | |
| 1.50 mm | 75.0 | -- | °C | |
| 3.00 mm | 75.0 | -- | °C | |
| RTI Str | | | | UL 746 |
| 0.400 mm | 75.0 | -- | °C | |
| 0.710 mm | 85.0 | -- | °C | |
| 1.50 mm | 85.0 | -- | °C | |
| 3.00 mm | 85.0 | -- | °C | |
| Электрический | Сухой | Состояние | Единица измерения | Метод испытания |
|---|
| Сопротивление громкости (0.750 mm) | 1.0E+13 | -- | ohms·cm | IEC 60093 |
| Диэлектрическая прочность (1.00 mm) | 26 | -- | kV/mm | IEC 60243 |
| Дуговое сопротивление (3.00 mm) | PLC 5 | -- | | ASTM D495 |
| Comparative Tracking Index (3.00 mm) | 600 | -- | V | IEC 60112 |
| Высокоусиленное дуговое зажигание (HAI) | | | | UL 746 |
| 0.400 mm | PLC 1 | -- | | |
| 0.710 mm | PLC 0 | -- | | |
| 1.50 mm | PLC 0 | -- | | |
| 3.00 mm | PLC 0 | -- | | |
| Высоковольтная скорость отслеживания дуги (HVTR) | PLC 0 | -- | | UL 746 |
| Зажигание горячей проволоки (HWI) | | | | UL 746 |
| 0.400 mm | PLC 4 | -- | | |
| 0.710 mm | PLC 4 | -- | | |
| 1.50 mm | PLC 3 | -- | | |
| 3.00 mm | PLC 2 | -- | | |
| Воспламеняемость | Сухой | Состояние | Единица измерения | Метод испытания |
|---|
| Огнестойкость | | | | UL 94 |
| 0.400 mm | V-2 | -- | | |
| 0.710 mm | V-2 | -- | | |
| 1.50 mm | V-2 | -- | | |
| 3.00 mm | V-2 | -- | | |
| Индекс воспламеняемости провода свечения | | | | IEC 60695-2-12 |
| 0.400 mm | 960 | -- | °C | |
| 0.710 mm | 960 | -- | °C | |
| 1.50 mm | 960 | -- | °C | |
| 3.00 mm | 960 | -- | °C | |
| Температура зажигания провода свечения | | | | IEC 60695-2-13 |
| 0.400 mm | 825 | -- | °C | |
| 0.710 mm | 850 | -- | °C | |
| 1.50 mm | 850 | -- | °C | |
| 3.00 mm | 850 | -- | °C | |
| Индекс кислорода | 26 | -- | % | ISO 4589-2 |
| Инъекция | Сухой | Единица измерения | |
|---|
| Температура сушки | < 70.0 | °C | |
| Время сушки | 1.0 to 3.0 | hr | |
| Рекомендуемый Макс измельчения | 50 | % | |
| Задняя температура | 260 to 280 | °C | |
| Средняя температура | 270 to 285 | °C | |
| Передняя температура | 280 to 290 | °C | |
| Температура сопла | 280 to 300 | °C | |
| Температура обработки (расплава) | 285 to 300 | °C | |
| Температура формы | 65.0 to 95.0 | °C | |