LUVOCOM® 1106-8600

Категория	PEI, Polyether Imide
Производитель	LEHVOSS Group
Торговая марка	LUVOCOM®
Порт	Китай Шанхайский порт
Торговые условия	FOB, CFR, CIF
Платежное средство	L/C, T/T, Western Union
PDF	EugLpO_LUVOCOM11068600.pdf
Контактная информация	EMAIL US  sales@su-jiao.com Служба поддержки клиентов Вичат

Описание материалов:

LUVOCOM®1106-8600 is a polyetherimide (PEI) material, and the filler is glass fiber reinforced material. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,.

LUVOCOM®The main features of 1106-8600 are:

Flame Retardant

Good stiffness

Главная Информация
Наполнитель/армирование	Армированный стекловолокном материал
Характеристики	Жесткий, хороший Хорошая прочность Огнестойкий
Внешний вид	Натуральный цвет

Физический	Номинальное значение	Единица измерения	Метод испытания
Плотность	1.51	g/cm³	ISO 1183
Формовочная усадка	0.15 - 0.35	%	DIN 16901
Поглощение воды (23°C, 24 hr)	< 0.30	%

Механические	Номинальное значение	Единица измерения	Метод испытания
Модуль растяжения	11000	MPa	ISO 527-2
Tensile Stress (Break)	175	MPa	ISO 527-2
Растяжимое напряжение (Yield)	2.1	%	ISO 527-2
Флекторный модуль	9500	MPa	ISO 178
Флекторный стресс	245	MPa	ISO 178
Flexural Strain at Flexural Strength	2.9	%	ISO 178

Тепловой	Номинальное значение	Единица измерения	Метод испытания
Максимальная рабочая температура- Короткий срок	200	°C

Электрический	Номинальное значение	Единица измерения	Метод испытания
Insulation Resistance	> 1.0E+12	ohms	IEC 60167

Воздействие	Номинальное значение	Единица измерения	Метод испытания
Charpy Unnotched Impact Strength (23°C)	44	kJ/m²	ISO 179/1eU

Тепловой	Номинальное значение	Единица измерения	Метод испытания
Heat Deflection Temperature (1.8 MPa, Unannealed)	205	°C	ISO 75-2/A
Температура непрерывного использования	170	°C	UL 746B
Викат Температура размягчения	220	°C	ISO 306/A
CLTE- Поток	2.0E-5	cm/cm/°C	DIN 53752

Электрический	Номинальное значение	Единица измерения	Метод испытания
Удельное сопротивление поверхности	> 1.0E+12	ohms	IEC 60093

Инъекция	Номинальное значение	Единица измерения
Температура сушки
Hot air dryer, A	120	°C
Hot air dryer, B	150	°C
Время сушки
Hot air dryer, A	> 8.0	hr
Hot air dryer, B	> 4.0	hr
Задняя температура	330 - 350	°C
Средняя температура	340 - 390	°C
Передняя температура	350 - 400	°C
Температура сопла	350 - 400	°C
Температура обработки (расплава)	380	°C
Температура формы	150 - 180	°C

Инструкции по впрыску
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.03%, otherwise porosity and surface defects (e.g. smearing) may occur. Predrying is recommended even when sealed original containers are being used. To avoid internal stresses, a low shear load should be used for processing. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. High-temperature polymers place increased demands on the tool steels employed. Please contact us for further information.

Инструкции по впрыску

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.03%, otherwise porosity and surface defects (e.g. smearing) may occur. Predrying is recommended even when sealed original containers are being used. To avoid internal stresses, a low shear load should be used for processing. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. High-temperature polymers place increased demands on the tool steels employed. Please contact us for further information.

Тип материала	Категория	Производитель
ULTEM™ 1100 resin	PEI	SABIC Innovative Plastics
ULTEM™ CRS5201R resin	PEI	SABIC Innovative Plastics
RTP 2107 Z	PEI	RTP Company
ULTEM™ HU2100 resin	PEI	SABIC Innovative Plastics
ULTEM™ CRS5201 resin	PEI	SABIC Innovative Plastics
LNP™ THERMOCOMP™ PDXE98480 compound	PEI	SABIC Innovative Plastics