Описание материалов:
Plexar tie-layers are chemically modified resins used to bond unlike materials, primarily in packaging and industrial applications. Common adherents include polyethylene resins and copolymers, EVA, EMA, polypropylene, polyamide (nylon), ethylene vinyl alcohol copolymers (EVOH), ionomer and other sealants, polyethylene terephthalate (PET) resins and copolymers, styrenic polymers, metal, and paperboard. Product grades primarily used for blown and cast films, sheet and thermoforming, blow molding, extrusion coating and lamination, tubing, pipe, and other specialty applications are available in pellet form. Contact your Plexar sales and/or Equistar technical service representative for more information and specific recommendations for your application(s).
| Главная Информация | |
|---|
| Используется | - Упаковка
- Промышленное применение
|
| Рейтинг агентства | - Управление по санитарному надзору за качеством пищевых продуктов и медикаментов 21 CFR 175,105
|
| Формы | |
| Метод обработки | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Плотность | 0.922 | g/cm³ | ASTM D1505 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 7.0 | g/10 min | ASTM D1238 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Толщина пленки протестирована | 51 | µm | |
| Прочность на растяжение | | | ASTM D882 |
| MD
: Yield, 51 µm, blown film | 11.0 | MPa | ASTM D882 |
| TD
: Yield, 51 µm, blown film | 8.70 | MPa | ASTM D882 |
| MD
: Broken, 51 µm, blown film | 17.7 | MPa | ASTM D882 |
| TD
: Broken, 51 µm, blown film | 13.7 | MPa | ASTM D882 |
| Удлинение при растяжении | | | ASTM D882 |
| MD
: yield, 51 µm, blow film | 21 | % | ASTM D882 |
| TD
: yield, 51 µm, blow film | 10 | % | ASTM D882 |
| MD
: Broken, 51 µm, blown film | 260 | % | ASTM D882 |
| TD
: Broken, 51 µm, blown film | 470 | % | ASTM D882 |
| Elmendorf Tear Strength | | | ASTM D1922 |
| MD
: 51 µm, blown film | 390 | g | ASTM D1922 |
| TD
: 51 µm, blown film | 180 | g | ASTM D1922 |
| Скорость передачи водяного пара (100% RH, 51 µm, Blown Film) | 7.4 | g/m²/24 hr | ASTM F372 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Викат Температура размягчения | 94.0 | °C | ASTM D1525 |
| Дополнительная информация |
|---|
| A process melt temperature above 410°F (210°C) is recommended to ensure adhesion between adherents. More specific suggestions can be made only when equipment, process parameters and conditions of use are known. |
| Экструзия | Номинальное значение | Единица измерения | |
|---|
| Температура расплава | > 210 | °C | |