TUFLIN™ HS-7028 NT 7
| Категория | LLDPE, Linear Low Density Polyethylene Resin |
| Производитель | The Dow Chemical Company |
| Торговая марка | TUFLIN™ |
| Порт | Китай Шанхайский порт |
| Торговые условия | FOB, CFR, CIF |
| Платежное средство | L/C, T/T, Western Union |
DrN2Nt_TUFLIN-HS-7028-NT-7.pdf  |
|
| Контактная информация |  Служба поддержки клиентов Вичат |
|
|
|
Описание материалов:
TUFLIN™ HS-7028 NT 7 Linear Low Density Polyethylene Resin is an ethylene-hexene copolymer, linear low density (LLDPE) resin designed for good strength and processability. This product is recommended for general purpose packaging applications from thick gauge, heavy duty bags to high speed thin gauge applications
Complies with:
- Hexene Linear Low Density Resin
- General Purpose Resin
- Excellent Strength
- An additive present in this product limits use only in film form for food contact applications.
Complies with:
- U.S. FDA 21 CFR 177.1520 (c) 3.1a (with Restrictions)
- European Commission Regulation (EU) No 10/2011
| Главная Информация | |
|---|---|
| Рейтинг агентства |
|
| Формы |
|
| Метод обработки |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Удельный вес | 0.918 | g/cm³ | ASTM D792 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Толщина пленки протестирована | 25 | µm | Internal method |
| Энергия прокола пленки | 4.52 | J | Internal method |
| Сила прокола пленки | 48.9 | N | Internal method |
| Сопротивление проколу пленки | 24.8 | J/cm³ | Internal method |
| Прочность пленки | ASTM D882 | ||
| MD | 82.7 | J/cm³ | ASTM D882 |
| TD | 82.7 | J/cm³ | ASTM D882 |
| Сектантный модуль | ASTM D882 | ||
| 1% secant, MD | 262 | MPa | ASTM D882 |
| 2% secant, MD | 214 | MPa | ASTM D882 |
| 1% secant, TD | 255 | MPa | ASTM D882 |
| 2% secant, TD | 214 | MPa | ASTM D882 |
| Прочность на растяжение | ASTM D882 | ||
| MD : Yield | 12.1 | MPa | ASTM D882 |
| TD : Yield | 11.7 | MPa | ASTM D882 |
| MD : Fracture | 37.9 | MPa | ASTM D882 |
| TD : Fracture | 37.9 | MPa | ASTM D882 |
| Удлинение при растяжении | ASTM D882 | ||
| MD : Fracture | 500 | % | ASTM D882 |
| TD : Fracture | 500 | % | ASTM D882 |
| Ударное падение Dart | 200 | g | ASTM D1709A |
| Elmendorf Tear Strength 1 | ASTM D1922 | ||
| MD | 380 | g | ASTM D1922 |
| TD | 600 | g | ASTM D1922 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Викат Температура размягчения | 109 | °C | ASTM D1525 |
| Температура плавления (DSC) | 124 | °C | Internal method |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Блеск (45°) | 34 | ASTM D2457 | |
| Haze | 18 | % | ASTM D1003 |
| Инструкции по экструзии |
|---|
| 吹塑薄膜的制造条件： 螺杆尺寸：3.5 英寸 (63.5 mm) 螺杆类型：DSBII 模具间隙：70 密尔 (1.8 mm) 熔体温度：415 °F 输出：模具周长的 12 磅/小时/英寸 模具直径：8 英寸 放大比：2.5 比 1 螺杆速度：39 rpm 冷冻线高度：57 英寸 |
| Примечание | |
|---|---|
| 1 . | Method B |
| Тип материала | Категория | Производитель |
|---|---|---|
| SureSpec LLSC6-007 | LLDPE | Genesis Polymers |
| TOTAL Polyethylene Lotrène® Q1018 H | LLDPE | TOTAL Refining & Chemicals |
| NEFTEKHIM PE 4431S (30405) | LLDPE | Nizhnekamskneftekhim Inc. |
| Exelene® LLDPE 1400 | LLDPE | Montachem International, Inc. |
| DOWLEX™ 2098P | LLDPE | The Dow Chemical Company |
| ICORENE® 3590 AS | LLDPE | A. Schulman Europe |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved