Clearflex H&T CMH 108 is an octene copolymer linear low density polyethylene (C8-LLDPE), with antioxidants, suitable for cast film extrusion.
Stretch films obtained from Clearflex H&T CMH 108 show excellent optical properties, high puncture and tear resistance along machine direction together with excellent performances in automatic wrapping machines (prestretch).
Main Application
Clearflex H&T CMH 108, for its rheological behaviour, is recommended in all special applications where ease of processing is a key issue. Moreover, thanks to a optimum combination between fracture mechanical properties (mainly puncture and MD Elmendorf tear resistance) and pre-stretch performances, Clearflex H&T CMH 108 is suggested to manufacture super power stretch cast film.
| Главная Информация | |
|---|
| Добавка | |
| Характеристики | - Антиоксидант
- Сополимер
- Приемлемый пищевой контакт
- Хорошая растяжимость
- Хорошая прочность на разрыв
- Низкая плотность
- Октеновый комномер
- Оптика
- Стойкий к проколу
|
| Используется | - Литая пленка
- Пленка
- Эластичная пленка
|
| Рейтинг агентства | - ЕС пищевой контакт, неуказанный рейтинг
|
| Формы | |
| Метод обработки | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Плотность | 0.920 | g/cm³ | ISO 1183 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 3.5 | g/10 min | ISO 1133 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Коэффициент трения (vs. Itself - Dynamic, Cast Film) | > 0.50 | | ISO 8295 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Толщина пленки протестирована | 23 | µm | |
| Толщина пленки-рекомендовано/доступно | 8 to 50µm | | |
| Модуль растяжения | | | ISO 527-3 |
| 1% Secant, MD
: 23 µm, Cast Film | 145 | MPa | |
| 1% Secant, TD
: 23 µm, Cast Film | 155 | MPa | |
| Tensile Stress | | | ISO 527-3 |
| MD
: Yield, 23 µm, Cast Film | 10.0 | MPa | |
| TD
: Yield, 23 µm, Cast Film | 10.0 | MPa | |
| MD
: Break, 23 µm, Cast Film | 42.0 | MPa | |
| TD
: Break, 23 µm, Cast Film | 35.0 | MPa | |
| Удлинение при растяжении | | | ISO 527-3 |
| MD
: Break, 23 µm, Cast Film | 600 | % | |
| TD
: Break, 23 µm, Cast Film | 800 | % | |
| Ударное падение Dart 1(23 µm, Cast Film) | 200 | g | ISO 7765-1 |
| Elmendorf Tear Strength 2 | | | ISO 6383-2 |
| MD
: 23.0 µm | 170.0 | kN/m | |
| TD
: 23.0 µm | 230.0 | kN/m | |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Температура ломкости | < -70.0 | °C | ASTM D746 |
| Викат Температура размягчения | 97.0 | °C | ISO 306/A |
| Температура плавления | 122 | °C | Internal Method |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Блеск (45°, 23.0 µm, Cast Film) | 93 | | ASTM D2457 |
| Haze (23.0 µm, Cast Film) | 0.50 | % | ISO 14782 |
| Экструзия | Номинальное значение | Единица измерения | |
|---|
| Температура расплава | 220 to 270 | °C | |
| Примечание |
|---|
| 1 . | F50 |
| 2 . | Cast Film |