EVATANE® 33-25 is a random copolymer of Ethylene and Vinyl Acetate made by high-pressure radicalar polymerization process.
The high Vinyl Acetate content of EVATANE® 33-25 brings softness, flexibility and polarity. EVATANE® 33-25 is compatible with most tackifying resins and waxes. It is an efficient and easy handling product for hot melt adhesives formulations. EVATANE® 33-25 delivers high cohesive strength with most fillers and can be used to produce HFFR compounds. It is also an ideal base polymer for semi-conductive compounds for medium voltage cables (external strippable layer).
| Главная Информация | |
|---|
| Характеристики | - Хорошая гибкость
- Случайный сополимер
- Мягкий
|
| Используется | - Клеи
- Применение проводов и кабелей
|
| Формы | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Плотность (23°C) | 0.960 | g/cm³ | ISO 1183 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 22 to 29 | g/10 min | ASTM D1238, ISO 1133 |
| Содержание винилацетата | 32.0 to 34.0 | wt% | Internal Method |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость дюрометра (Shore A) | 67 | | ASTM D2240, ISO 868 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Прочность на растяжение (Break) | 11.0 | MPa | ASTM D638, ISO 527-2 |
| Удлинение при растяжении (Break) | 900 to 1100 | % | ASTM D638, ISO 527-2 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Викат Температура размягчения | < 40.0 | °C | ISO 306/A, ASTM D1525 1 |
| Температура плавления | 63.0 | °C | ISO 11357-3 |
| Ring and Ball Softening Point 2 | 119 | °C | ASTM E28 |
| Примечание |
|---|
| 1 . | Loading 1 (10 N) |
| 2 . | NF EN 1238 |