- Главная страница
- Поиск продуктов
- EVA
- ELEVATE™ EF545
ELEVATE™ EF545
| Категория | EVA, Ethylene Vinyl Acetate Copolymer |
| Производитель | Westlake Chemical Corporation |
| Торговая марка | ELEVATE™ |
| Порт | Китай Шанхайский порт |
| Торговые условия | FOB, CFR, CIF |
| Платежное средство | L/C, T/T, Western Union |
GpXdbc_ELEVATE-EF545.pdf  |
|
| Контактная информация |  Служба поддержки клиентов Вичат |
|
|
|
Описание материалов:
Westlake EF545AW resin is a 4.0% VA ethylene vinyl acetate copolymer with high antiblock designed for stretch and other film applications where cold temperature performance and low C.O.F. are needed. This grade provides reasonable optics even with the high antiblock loading necessary to achieve the low C.O.F. Excellent cold temperature performance, toughness, and resistance to load deformation make EF545AW a wise selection for wrapping pallets stored in food freezers and other cold environments.
Application/Uses:
Pallet wrap stretch film
Food packaging stretch film
Application/Uses:
Pallet wrap stretch film
Food packaging stretch film
| Главная Информация | |
|---|---|
| Характеристики |
|
| Используется |
|
| Рейтинг агентства |
|
| Метод обработки |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Плотность | 0.931 | g/cm³ | ASTM D1505 |
| Массовый расход расплава (MFR) | 0.55 | g/10 min | ASTM D1238 |
| Содержание винилацетата | 4.0 | wt% |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Коэффициент трения (Blown Film) | 0.50 | ASTM D1894 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Толщина пленки протестирована | 38 | µm | |
| Сектантный модуль 1 | ASTM D882 | ||
| 1% secant, MD : 38 µm, blown film | 166 | MPa | ASTM D882 |
| 1% secant, TD : 38 µm, blown film | 200 | MPa | ASTM D882 |
| Прочность на растяжение 2 | ASTM D882 | ||
| MD : Broken, 38 µm, blown film | 22.0 | MPa | ASTM D882 |
| TD : Broken, 38 µm, blown film | 17.0 | MPa | ASTM D882 |
| Удлинение при растяжении 3 | ASTM D882 | ||
| MD : Broken, 38 µm, blown film | 230 | % | ASTM D882 |
| TD : Broken, 38 µm, blown film | 600 | % | ASTM D882 |
| Ударное падение Dart 4(38 µm, Blown Film) | 160 | g | ASTM D1709 |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Блеск (45°, 38.1 µm, Blown Film) | 50 | ASTM D2457 | |
| Haze (38.1 µm, Blown Film) | 13 | % | ASTM D1003 |
| Дополнительная информация |
|---|
| Test specimens for blown film: nominal thickness 1.5 mils; blow up ratio 2.4:1, die gap 35 mils. |
| Примечание | |
|---|---|
| 1 . | Test run at 23°C (73°F) and 50% relative humidity |
| 2 . | Test run at 23°C (73°F) and 50% relative humidity |
| 3 . | Test run at 23°C (73°F) and 50% relative humidity |
| 4 . | Test run at 23°C (73°F) and 50% relative humidity |
| Тип материала | Категория | Производитель |
|---|---|---|
| DENKA EVA TEX 70 | EVA | Denka Company Limited |
| Elvax® 410 | EVA | DuPont Packaging & Industrial Polymers |
| HANWHA EVA 1326 | EVA | Hanwha Chemical |
| Escorene™ Ultra UL 12530CC | EVA | ExxonMobil Chemical |
| Escorene™ Ultra UL 15019CC | EVA | ExxonMobil Chemical |
| Escorene™ Ultra UL 00112 | EVA | ExxonMobil Chemical |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved