Описание материалов:
Baydur 742 IBS is a semirigid polyurethane structural foam system used in the reaction injection molding (RIM) process. This system incorporates a specially engineered interactive blowing system (IBS) and is supplied as two reactive liquid components. Component A is a modified polymeric diphenylmethane diisocyanate (PMDI) prepolymer blend, and Component B is a formulated polyol system containing no CFC- or HCFC-blowing additives.
Baydur 742 IBS system is used in the consumer products market for applications requiring some protective cushioning characteristics. The system is typically molded at medium-to-high densities. As with any product, use of the Baydur 742 IBS system in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability.
| Главная Информация | |
|---|
| Добавка | |
| Используется | |
| Метод обработки | - Литье под давлением реакции (обод)
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 0.509 | g/cm³ | ASTM D792 |
| Формовочная усадка-
Поток (12.7 mm) | 0.90 to 1.1 | % | ASTM D955 |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость дюрометра (Shore D, 12.7 mm) | 41 | | ASTM D2240 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Прочность на растяжение (Break, 12.7 mm) | 6.55 | MPa | ASTM D638 |
| Удлинение при растяжении (Break, 12.7 mm) | 130 | % | ASTM D638 |
| Флекторный модуль (12.7 mm) | 118 | MPa | ASTM D790 |
| Flexural Strength (12.7 mm) | 6.55 | MPa | ASTM D790 |
| Прочность на сжатие (12.7 mm) | 1.48 | MPa | ASTM D695 |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Charpy Unnotched Impact Strength 1 | No Break | | Internal Method |