Описание материалов:
Andur M-22 is an MDI-Ester prepolymer that, when processed with close attention to handling procedures and formulation, produces high quality elastomers. These elastomers perform very well in dynamic applications.
| Твердость | Номинальное значение | | Метод испытания |
|---|
| Твердость дюрометра | | | ASTM D2240 |
| Shaw A | 60 | | ASTM D2240 |
| Shaw D | 15 | | ASTM D2240 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Прочность на сжатие | | | ASTM D695 |
| 2% strain | 0.172 | MPa | ASTM D695 |
| 5% strain | 0.345 | MPa | ASTM D695 |
| 10% strain | 0.621 | MPa | ASTM D695 |
| 15% strain | 0.896 | MPa | ASTM D695 |
| 20% strain | 1.24 | MPa | ASTM D695 |
| 25% strain | 1.65 | MPa | ASTM D695 |
| 50% strain | 5.52 | MPa | ASTM D695 |
| Устойчивость к истиранию | 3.50 | mg | ASTM D1044 |
| Эластомеры | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Tensile Stress | | | ASTM D412 |
| 100% strain | 1.38 | MPa | ASTM D412 |
| 300% strain | 1.55 | MPa | ASTM D412 |
| Прочность на растяжение (Yield) | 16.2 | MPa | ASTM D412 |
| Удлинение при растяжении (Break) | 720 | % | ASTM D412 |
| Комплект сжатия | 27 | % | ASTM D395 |
| Термокомплект | Номинальное значение | Единица измерения | |
|---|
| Срок службы горшка | 7.0 - 10 | min | |
| Время демолд | 90 | min | |
| Дополнительная информация |
|---|
| Die C Tear, ASTM D1004: 160 pliAverage Split Tear, ASTM D1938: 95 pliStoichiometry Curative Level: 97%Break Set, ASTM D412-80: 50%NBS Abrasion: 180% Rubber StandardParts of curative per 100 parts Andur M-22, 6.5% NCO: 11.26 parts by weightParts of curative per 100 parts Andur M-22, 6.55% NCO: 11.36 parts by weightParts of curative per 100 parts Andur M-22, 6.6% NCO: 11.44 parts by weightParts of curative per 100 parts Andur M-22, 6.65% NCO: 11.53 parts by weightParts of curative per 100 parts Andur M-22, 6.7% NCO: 11.62 parts by weightMix Temperature:
Andur M-22: 194-212°F
Curative TEG: 77-158 °F
Stability:
Ambient Temperature, 25°C: 6 Months
Melting Temperature, 60°C: 1 Month
Processing Temperature, 90°C: 12 Hours
Processing Temperature, 105°C: 3 Hours |
| Инъекция | Номинальное значение | Единица измерения | |
|---|
| Температура формы | 90.0 - 120 | °C | |