Описание материалов:
Clearflex H&T LFH 238 is an octene copolymer linear low density polyethylene (C8-LLDPE), with antioxidants and processing aid, suitable for blown film extrusion. It contains slip and antiblocking agents.
Films obtained from Clearflex H&T LFH 238 have excellent optical properties (haze and gloss), wide sealing temperature window, together with optimal sealing behaviour, outstanding tear, impact and puncture resistance. Its properties make Clearflex H&T LFH 238 the right chois for top end performance applications.
Main Application
Due to its excellent sealing properties, Clearflex H&T LFH 238 is recommended for packaging of food and edible fats and for applications requiring a superior sealing performance. Its very low gel content makes it ideal for lamination.
| Главная Информация | |
|---|
| Добавка | - Антиблок
- Антиоксидант
- Обработка помощи
- Комбинация
|
| Характеристики | - Антиблокировка
- Антиоксидант
- Широкий диапазон уплотнения
- Сополимер
- Приемлемый пищевой контакт
- Хорошее тепловое уплотнение
- Хорошая прочность на разрыв
- Глянцевый
- Высокая ударопрочность
- Низкая плотность
- Низкий гель
- Октеновый комномер
- Оптика
- Стойкий к проколу
- Комбинация
|
| Используется | - Пленка
- Пищевая упаковка
- Ламинаты
|
| Рейтинг агентства | - ЕС пищевой контакт, неуказанный рейтинг
|
| Формы | |
| Метод обработки | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Плотность | 0.920 | g/cm³ | ISO 1183 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 0.75 | g/10 min | ISO 1133 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Коэффициент трения (vs. Itself - Dynamic, Blown Film) | 0.12 | | ISO 8295 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Толщина пленки протестирована | 25 | µm | |
| Толщина пленки-рекомендовано/доступно | 10 to 50µm | | |
| Модуль растяжения | | | ISO 527-3 |
| 1% Secant, MD
: 25 µm, Blown Film | 200 | MPa | |
| 1% Secant, TD
: 25 µm, Blown Film | 250 | MPa | |
| Tensile Stress | | | ISO 527-3 |
| MD
: Yield, 25 µm, Blown Film | 10.0 | MPa | |
| TD
: Yield, 25 µm, Blown Film | 10.0 | MPa | |
| MD
: Break, 25 µm, Blown Film | 50.0 | MPa | |
| TD
: Break, 25 µm, Blown Film | 45.0 | MPa | |
| Удлинение при растяжении | | | ISO 527-3 |
| MD
: Break, 25 µm, Blown Film | 600 | % | |
| TD
: Break, 25 µm, Blown Film | 750 | % | |
| Ударное падение Dart 1(25 µm, Blown Film) | 250 | g | ISO 7765-1 |
| Elmendorf Tear Strength 2 | | | ISO 6383-2 |
| MD
: 25.0 µm | 180.0 | kN/m | |
| TD
: 25.0 µm | 250.0 | kN/m | |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Температура ломкости | < -70.0 | °C | ASTM D746 |
| Викат Температура размягчения | 102 | °C | ISO 306/A |
| Температура плавления | 119 | °C | Internal Method |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Блеск (45°, 25.0 µm, Blown Film) | 60 | | ASTM D2457 |
| Haze (25.0 µm, Blown Film) | 11 | % | ISO 14782 |
| Экструзия | Номинальное значение | Единица измерения | |
|---|
| Температура расплава | 190 to 230 | °C | |
| Примечание |
|---|
| 1 . | F50 |
| 2 . | Blown Film |