Описание материалов:
The PETROTHENE SELECT series of resins are pelletized, high performance hexene, linear low density polyethylenes for applications requiring superior strength and toughness. These products offer significant improvements in mechanical properties and excellent additive homogeneity without sacrificing processability compared to conventional Hexene LLDPE materials. GS 710 exhibits superior processability compared to competitive High Performance Hexene LLDPE materials. Applications include trash and can liners, commercial and industrial packaging, as well as consumer packaging. The PETROTHENE SELECT series resins offer enhanced film strength, drawdown, toughness and heat seal strength.
| Главная Информация | |
|---|
| Характеристики | - Гексен-комномер
- Обрабатываемость, хорошая
- Хорошее Отшелушивание
- Хорошая прочность
- Хорошее уплотнение тепла
- Хорошая прочность
- Соответствие пищевого контакта
|
| Используется | - Упаковка
- Подкладка
- Промышленное применение
|
| Рейтинг агентства | - FDA 21 CFR 177,1520 (c) 3.1a
|
| Формы | |
| Метод обработки | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Плотность | 0.924 | g/cm³ | ASTM D1505 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Толщина пленки протестирована | 25 | µm | |
| Сектантный модуль | | | ASTM D882 |
| 1% secant, MD
: 25 µm | 193 | MPa | ASTM D882 |
| 1% secant, TD
: 25 µm | 200 | MPa | ASTM D882 |
| Прочность на растяжение | | | ASTM D882 |
| MD
: Break, 25 µm | 55.2 | MPa | ASTM D882 |
| TD
: Break, 25 µm | 41.4 | MPa | ASTM D882 |
| Удлинение при растяжении | | | ASTM D882 |
| MD
: Break, 25 µm | 580 | % | ASTM D882 |
| TD
: Break, 25 µm | 720 | % | ASTM D882 |
| Ударное падение Dart (25 µm, Blown Film) | 600 | g | ASTM D1709A |
| Elmendorf Tear Strength | | | ASTM D1922 |
| MD
: 25 µm | 350 | g | ASTM D1922 |
| TD
: 25 µm | 580 | g | ASTM D1922 |
| Дополнительная информация |
|---|
| Film properties taken from blown film produced on a blown film line equipped with an 8 in diameter die and 100 mil die gap, running at 150 lb/hr and 420°F melt temperature.Density of Base Resin, ASTM D1505: 0.915 g/cm³Density of Compound, ASTM D1505: 0.924 g/cm³ |
| Экструзия | Номинальное значение | Единица измерения | |
|---|
| Температура расплава | 204 - 232 | °C | |