ATTANE™ NG 4701G
| Категория | ULDPE, Ultra Low Density Polyethylene Resin |
| Производитель | The Dow Chemical Company |
| Торговая марка | ATTANE™ |
| Порт | Китай Шанхайский порт |
| Торговые условия | FOB, CFR, CIF |
| Платежное средство | L/C, T/T, Western Union |
AeVAgv_ATTANE-NG-4701G.pdf  |
|
| Контактная информация |  Служба поддержки клиентов Вичат |
|
|
|
Описание материалов:
ATTANE™ NG 4701G Polyethylene Resin is a great abuse resistance copolymer offering extremely high impact strength, combined with good tear and exceptional optics. It has the added benefit of being easy to process (low melt temperature, low extruder amps and low screen pack backpressure) which translates into quality film rolls due to its bubble stability.
Main Characteristics:
Complies with:
Main Characteristics:
- Ultra low density ethylene/octene copolymer
- High performance film applications
Complies with:
- U.S. FDA 21 CFR 177.1520(c)3.2a.
- Canadian HPFB No Objection
| Главная Информация | |
|---|---|
| Рейтинг агентства |
|
| Формы |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Удельный вес | 0.912 | g/cm³ | ASTM D792 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 0.80 | g/10 min | ASTM D1238 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Толщина пленки протестирована | 25 | µm | |
| Энергия прокола пленки | 6.21 | J | Internal method |
| Сила прокола пленки | 71.2 | N | Internal method |
| Сопротивление проколу пленки | 33.1 | J/cm³ | Internal method |
| Прочность пленки | ASTM D882 | ||
| MD | 72.8 | J/cm³ | ASTM D882 |
| TD | 70.3 | J/cm³ | ASTM D882 |
| Сектантный модуль | ASTM D882 | ||
| 1% secant, MD | 141 | MPa | ASTM D882 |
| 2% secant, MD | 124 | MPa | ASTM D882 |
| 1% secant, TD | 148 | MPa | ASTM D882 |
| 2% secant, TD | 131 | MPa | ASTM D882 |
| Прочность на растяжение | ASTM D882 | ||
| MD : Yield | 8.96 | MPa | ASTM D882 |
| TD : Yield | 8.62 | MPa | ASTM D882 |
| MD : Fracture | 41.4 | MPa | ASTM D882 |
| TD : Fracture | 37.2 | MPa | ASTM D882 |
| Удлинение при растяжении | ASTM D882 | ||
| MD : Fracture | 400 | % | ASTM D882 |
| TD : Fracture | 450 | % | ASTM D882 |
| Ударное падение Dart | 380 | g | ASTM D1709B |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD | 250 | g | ASTM D1922 |
| TD | 600 | g | ASTM D1922 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Викат Температура размягчения | 99.0 | °C | ASTM D1525 |
| Температура плавления (DSC) | 101 | °C | ISO 3146 |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Блеск (45°) | 49 | ASTM D2457 | |
| Haze | 11 | % | ASTM D1003 |
| Инструкции по экструзии |
|---|
| 吹塑薄膜的制造条件： 螺杆尺寸：3.5 in. 螺杆类型：DSBII 模具间隙：70 密尔 (1.8 mm) 输出：模具周长的 12 磅/小时/英寸 模具直径：8 英寸 放大比：2.5:1 冷冻线高度：39 英寸。 |
| Тип материала | Категория | Производитель |
|---|---|---|
| Generic ULDPE | ULDPE | Generic |
| Lumitac® Lumitac® | ULDPE | TOSOH Corporation |
| ATTANE™ 4607GC | ULDPE | The Dow Chemical Company |
| ATTANE™ 4203 | ULDPE | The Dow Chemical Company |
| ATTANE™ 4201G | ULDPE | The Dow Chemical Company |
| ATTANE™ NG 4701G | ULDPE | The Dow Chemical Company |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved