Описание материалов:
Menzolit® BMC 3100 is a bulk moulding compound based on unsaturated polyester resin. The product is glass fibre reinforced and contains mineral fillers. In case of fire the product doesn't melt, neither does it form droplets nor is smoke generation excessive. The material is injection moulded in heated steel moulds. It is recommended to work with chrome plated tools. The product contains no halogens.
Menzolit® BMC 3100 is a special BMC suitable for the use in head lamp reflectors. Because of its high temperature resistance and dimensional stability as well as low coefficient of thermal expansion, complex shapes and good reflective properties can be made. Because of its temperature resistance the precise geometry of the reflector will keep its precise shape even at high temperature. It has found specific use in the field of reflectors for automotive head lamps but its use as lamp housings for household and office lighting equipment is possible as well.
| Главная Информация | |
|---|
| Наполнитель/армирование | - Стекло минеральное, 12% наполнитель по весу
|
| Характеристики | - Огнестойкий
- Хорошая стабильность размеров
- Без галогенов
- Высокая термостойкость
- Низкий уровень дыма
|
| Используется | - Автомобильные Приложения
- Корпуса
- Отражатели
|
| Внешний вид | |
| Формы | |
| Метод обработки | |
| Код маркировки деталей (ISO 11469) | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Плотность | 2.00 | g/cm³ | ISO 1183 |
| Формовочная усадка | | | |
| -- | -0.030 | % | ISO 2577 |
| -- 1 | 0.0 | % | DIN 53464 |
| Поглощение воды (Saturation, 23°C) | < 0.50 | % | ISO 62 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Модуль растяжения (Compression Molded) | 14000 | MPa | ISO 527-2 |
| Tensile Stress (Yield, Compression Molded) | 25.0 | MPa | ISO 527-2 |
| Растяжимое напряжение (Break, Compression Molded) | 1.0 | % | ISO 527-2 |
| Флекторный модуль (Compression Molded) | 11000 | MPa | ISO 178 |
| Флекторный стресс (Compression Molded) | 79.0 | MPa | ISO 178 |
| Poisson's Ratio | 0.30 | | Internal Method |
| Matrix Crazing Strain | 0.30 | % | Internal Method |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Ударная прочность (Compression Molded) | 15 | kJ/m² | ISO 179 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | > 150 | °C | ISO 75-2/A |
| Температура непрерывного использования | 190 | °C | Internal Method |
| Температура перехода стекла | 185 | °C | DSC |
| CLTE-
Поток | 1.0E-5 | cm/cm/°C | ISO 11359-2 |
| Воспламеняемость | Номинальное значение | | Метод испытания |
|---|
| Огнестойкость (2.00 mm) | HB | | UL 94 |
| Инъекция | Номинальное значение | Единица измерения | |
|---|
| Температура формы | 135 to 160 | °C | |
| Давление впрыска | 2.00 to 8.00 | MPa | |
| Примечание |
|---|
| 1 . | Post Molding Shrinkage |
| Тип материала |
Категория |
Производитель |
|
Generic Polyester, TS - Glass\Mineral |
Polyester, TS |
Generic
|
|
En Chuan 6120 |
Polyester, TS |
En Chuan Chemical Industries Co,. Ltd.
|
|
Premi-Glas® 3100-20 |
TS, Unspecified |
Premix, Inc.
|
|
Menzolit® BMC 0410 |
Polyester, TS |
Menzolit Ltd (UK)
|
|
BMC 610 |
Polyester, TS |
Bulk Molding Compounds, Inc.
|
|
Haysite Plastics H900 |
Polyester, TS |
Haysite Reinforced Plastics
|