Описание материалов:
APTIV® 1100 series films are the mineral filled semi-crystalline films made from VICTREX® PEEK™ polymer. The film provides a material solution for engineers in ultra-high performance applications.
APTIV films are a comprehensive range of versatile, high-performance films, the use of which can facilitate reduced systems costs, improved performance and enhanced design freedom.
APTIV 1100 has a unique combination of properties providing high temperature performance, mechanical strength, durability, excellent radiation, hydrolysis and chemical resistance, electrical insulation, excellent barrier properties with high purity, good flammability without the use of flame retardants, low toxicity of combustion products, and low moisture absorption in a film format. Inherently halogen free and ease of processing makes APTIV films a technology enabler for our customers and end users. APTIV 1100 series provides a higher modulus and lower coefficient of linear thermal expansion over the APTIV 1000 series.
| Главная Информация | |
|---|
| Наполнитель/армирование | - Минеральный, 20% наполнитель по весу
|
| Характеристики | - Барьерная смола
- Чистота/Высокая чистота
- Прочный
- Электрически изолирующий
- Отличная Печатающая способность
- Огнестойкий
- Хорошая адгезия
- Хорошая химическая стойкость
- Хорошая технологичность
- Хорошая прочность
- Без галогенов
- Термогерметичный
- Высокая термостойкость
- Высокая прочность
- Устойчивость к гидролизу
- Лазерная разметка
- Низкое поглощение влаги
- Низкий уровень дыма
- Низкая токсичность
- Обрабатываемый
- Металлизируемый
- Устойчивость к излучению (гамма)
- Перерабатываемый материал
- Полукристаллический
- Свариваемый
|
| Используется | - Диафрагмы
- Электрическое/электронное применение
- Пленка
- Изоляция
- Этикетки
- Ламинаты
- Мембраны
- Печатные платы
|
| Рейтинг агентства | - ЕС 2002/72/ЕС
- ЕС 2004/19/ЕС
- Управление по санитарному надзору за качеством пищевых продуктов и медикаментов 21 CFR 177,2415
|
| Соответствие RoHS | |
| Внешний вид | |
| Формы | |
| Метод обработки | - Покрытие
- Ламинирование
- Термоформовка
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Плотность (23°C) | 1.45 | g/cm³ | ISO 1183 |
| Поглощение воды 1(Equilibrium, 23°C, 0.0500 mm, 50% RH) | 0.080 | % | ISO 62 |
| Усадка 2 | | | |
| MD
: 200°C, 50.0 µm | < 0.50 | % | |
| TD
: 200°C, 50.0 µm | < 0.50 | % | |
| Дополнительная информация | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Сопротивление проколу (23 °C, 50,0 мкм) | 5.00 | kJ/m² | Internal Method |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Толщина пленки-рекомендовано/доступно | 25 to 125 µm | | |
| Модуль растяжения | | | ISO 527-3 |
| MD
: 23°C, 25 µm | 5000 | MPa | |
| TD
: 23°C, 25 µm | 4500 | MPa | |
| MD
: 23°C, 50 µm | 4800 | MPa | |
| TD
: 23°C, 50 µm | 4300 | MPa | |
| MD
: 23°C, 100 µm | 4500 | MPa | |
| TD
: 23°C, 100 µm | 4200 | MPa | |
| Tensile Stress | | | ISO 527-3 |
| MD
: Break, 23°C, 25 µm | 100 | MPa | |
| TD
: Break, 23°C, 25 µm | 80.0 | MPa | |
| MD
: Break, 23°C, 50 µm | 100 | MPa | |
| TD
: Break, 23°C, 50 µm | 80.0 | MPa | |
| MD
: Break, 23°C, 100 µm | 100 | MPa | |
| TD
: Break, 23°C, 100 µm | 80.0 | MPa | |
| Удлинение при растяжении | | | ISO 527-3 |
| MD
: Break, 23°C, 25 µm | > 100 | % | |
| TD
: Break, 23°C, 25 µm | > 10 | % | |
| MD
: Break, 23°C, 50 µm | > 100 | % | |
| TD
: Break, 23°C, 50 µm | > 10 | % | |
| MD
: Break, 23°C, 100 µm | > 100 | % | |
| TD
: Break, 23°C, 100 µm | > 10 | % | |
| Сопротивление разрыву брюк 3 | | | ISO 6383-1 |
| MD
: 50 µm | 6.00 | N/mm | |
| TD
: 50 µm | 7.00 | N/mm | |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| CLTE-
Поток 4(0.0500 mm) | 3.5E-5 | cm/cm/°C | ASTM D696 |
| Теплопроводность | | | ASTM E1461 |
| -- 5 | 0.43 | W/m/K | |
| -- 6 | 0.91 | W/m/K | |
| Электрический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Сопротивление громкости 7(23°C, 0.0500 mm) | 1.0E+16 | ohms·cm | ASTM D257 |
| Диэлектрическая прочность (23°C, 0.0500 mm) | 200 | kV/mm | ASTM D149 |
| Диэлектрическая постоянная (23°C, 0.0500 mm, 10 MHz) | 3.60 | | ASTM D150 |
| Коэффициент рассеивания (23°C, 0.0500 mm, 10 MHz) | 1.0E-3 | | ASTM D150 |
| Примечание |
|---|
| 1 . | 24 hrs, 23°C |
| 2 . | TM-VX-84 |
| 3 . | 23°C |
| 4 . | below Tg |
| 5 . | Through Plane |
| 6 . | In-Plane |
| 7 . | 100 V |